Braskem IE59U3 HDPE Injection Molding Polyethylene Homopolymer

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded
Manufacturer Braskem
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem IE59U3 HDPE Injection Molding Polyethylene Homopolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
IE59U3 is a high-density polyethylene, narrow molecular weight homopolymer produced by the solution process for injection molding applications. It offers high stiffness and impact strength, good processability, and low warpage. It contains light stabilizer and antioxidant additives. Its applications include: large containers, technical articles with high mechanical and weathering resistance, buckets, trash containers, crates, and safety helmets. IE59U3 has been developed for injection molding under conditions comparable to high-density polyethylene with a similar melt flow index. Recommended temperature profile: 160 to 230ºC.
Physical Properties Metric English Comments
Density 0.959 g/cc
0.0346 lb/in³
ASTM-D792
ESCR 10% Igepal® <= 4.0 hour

@Thickness 2.00 mm,
Temperature 50.0 °C
<= 4.0 hour

@Thickness 0.0787 in,
Temperature 122 °F
0.3 mm notched-plaques; ASTM-D1693
Melt Flow 5.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
5.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM-D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 57
57
ASTM-D2240
Tensile Strength at Break 26.0 MPa
3770 psi
ASTM-D638
Tensile Strength, Yield 28.0 MPa
4060 psi
ASTM-D638
Flexural Modulus, 1% Secant 1200 MPa
174000 psi
ASTM-D790
Izod Impact, Notched 0.850 J/cm
1.59 ft-lb/in
ASTM-D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 74.0 °C
165 °F
ASTM-D648
Vicat Softening Point 129 °C

@Load 1.02 kg
264 °F

@Load 2.25 lb
ASTM-D1525