Braskem INSPIRE™ 114 Performance Polypropylene Polymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Blow Molding Grade , Polypropylene, Extrusion Grade , Polypropylene, Impact Modified; Molded/Extruded , Polypropylene, Sheet/Thermoforming Grade
Manufacturer Braskem
Trade Name INSPIRE™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem INSPIRE™ 114 Performance Polypropylene Polymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
OverviewHigh melt strengthHigh toughnessExcellent processabilityHigh impact and puncture resistanceHigh film stiffness/machinabilityHigh heat resistanceComplies with U.S. FDA FCN 843, Europe EU-Directive 2002/72/ECINSPIRE™ 144 Performance Polymer is intended for use in blown film extrusion. Film produced from this resin offers improved stiffness, heat resistance, creep resistance, puncture strength and toughness over competitive polyethylene films. Coextruded structures offer a broad range of potential properties including high stiffness, high clarity, excellent sealability and good barrier properties. INSPIRE 114 Performance Polymer offers high output rates, thin or thick film production with excellent bubble stability, and good gauge uniformity.INSPIRE™ 114 Performance Polymer is a propylene-based resin that is also intended for use in sheet extrusion, thermoforming, and blow molding.This product line was spun off from Dow Chemical to Braskem
Physical Properties Metric English Comments
Density 0.900 g/cc
0.0325 lb/in³
ASTM D792
Thickness 50.8 microns
2.00 mil
Film Thickness
Melt Index of Compound 0.50 g/10 min

@Load 2.16 kg,
Temperature 230 °C
0.50 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 30.8 MPa
4470 psi
50.8 microns, Blown Film; ASTM D882
Film Tensile Strength at Yield, TD 25.2 MPa
3650 psi
50.8 microns, Blown Film; ASTM D882
Tensile Strength, Yield 30.0 MPa
4350 psi
ASTM D638
Film Elongation at Break, MD 700 %
700 %
50.8 microns, Blown Film; ASTM D882
Film Elongation at Break, TD 850 %
850 %
50.8 microns, Blown Film; ASTM D882
Film Elongation at Yield, MD 14 %
14 %
50.8 microns, Blown Film; ASTM D882
Film Elongation at Yield, TD 12 %
12 %
50.8 microns, Blown Film; ASTM D882
Elongation at Yield 12 %
12 %
ASTM D638
Flexural Modulus, 1% Secant 1480 MPa
215000 psi
ASTM D790A
Secant Modulus, MD 0.896 GPa
130 ksi
2% secant modulus; ASTM D882
Secant Modulus, TD 0.772 GPa
112 ksi
2% secant modulus; ASTM D882
Izod Impact, Notched NB
NB
ASTM D256A
Dart Drop Test 120 g
0.265 lb
50.8 microns, Blown Film; ASTM D1709A
Film Tensile Strength at Break, MD 47.9 MPa
6950 psi
50.8 microns, Blown Film; ASTM D882
Film Tensile Strength at Break, TD 36.9 MPa
5350 psi
50.8 microns, Blown Film; ASTM D882
Thermal Properties Metric English Comments
Melting Point 164 °C
327 °F
DSC; Dow Method