Braskem INSPIRE™ 137 NA Performance Polypropylene Polymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene, Blow Molding Grade , Polypropylene, Extrusion Grade , Polypropylene, Film Grade , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer Braskem
Trade Name INSPIRE™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem INSPIRE™ 137 NA Performance Polypropylene Polymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
INSPIRE™ 137 Performance polymer is an impact copolymer, primarily designed for film extrusion and suitable for blow molding where high mechanical properties are of the highest importance.INSPIRE 137 Performance Polymer is a high molecular weight, high impact copolymer with a broad molecular weight distribution.ApplicationsFilmSheet and boardsAdhesive tapePaper laminationExtrusion profiles and pipesDrainage and sewage pipesBlow molded containers (detergents, toiletries, foodstuffs)Complies with US FDA FCN 843This product line was spun off from Dow Chemical to Braskem
Physical Properties Metric English Comments
Density 0.900 g/cc
0.0325 lb/in³
ISO 1183
Melt Index of Compound 0.80 g/10 min

@Load 2.16 kg,
Temperature 230 °C
0.80 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 24.0 MPa
3480 psi
Injection Molded; ISO 527-2
Elongation at Yield 15 %
15 %
Injection Molded; ASTM D638
Flexural Modulus 1.00 GPa
145 ksi
Injection Molded; ISO 178
Charpy Impact, Notched 8.00 J/cm²

@Temperature -20.0 °C
38.1 ft-lb/in²

@Temperature -4.00 °F
Injection Molded; ISO 75-2/B
12.0 J/cm²

@Temperature 0.000 °C
57.1 ft-lb/in²

@Temperature 32.0 °F
Injection Molded; ISO 75-2/B
55.0 J/cm²

@Temperature 23.0 °C
262 ft-lb/in²

@Temperature 73.4 °F
Injection Molded; ISO 75-2/B
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 85.0 °C
185 °F
Unannealed; IDO 75-2/B
Vicat Softening Point 146 °C
295 °F
ISO 306/A