Braskem LL3800N HDPE Cast Film Extrusion Polyethylene Copolymer

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer Braskem
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem LL3800N HDPE Cast Film Extrusion Polyethylene Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The resin LL3800N is a high-density polyethylene, copolymer octene-1, produced by the solution process for the extrusion of plain films with excellent mechanical properties. It has an antirust additive. Its applications include: extrusion of plain films for diapers; hygienic absorbers; and other specialties. LL3800N is indicated for the processing in a plain die extruding machine in conditions that are similar to the other types of high-density linear polyethylene of equivalent fluidity and density. Recommended temperature range: 250 to 290 °C.
Physical Properties Metric English Comments
Density 0.943 g/cc
0.0341 lb/in³
ASTM-D792
Melt Flow 4.9 g/10 min

@Load 2.16 kg,
Temperature 190 °C
4.9 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM-D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 1320 %
1320 %
ASTM-D882
Film Elongation at Break, TD 740 %
740 %
ASTM-D882
Elmendorf Tear Strength MD 20 g
20 g
ASTM-D1922
Elmendorf Tear Strength TD 30 g
30 g
ASTM-D1922
Elmendorf Tear Strength, MD 0.800 g/micron
20.3 g/mil
ASTM-D1922
Elmendorf Tear Strength, TD 1.20 g/micron
30.5 g/mil
ASTM-D1922
Film Tensile Strength at Break, MD 30.0 MPa
4350 psi
ASTM-D882
Film Tensile Strength at Break, TD 20.0 MPa
2900 psi
ASTM-D882
1% Secant Modulus, MD 450 MPa
65300 psi
ASTM-D882
1% Secant Modulus, TD 160 MPa
23200 psi
ASTM-D882
Optical Properties Metric English Comments
Haze 75 %
75 %
ASTM-D1003
Gloss 12 %
12 %
Angle 60°; ASTM-D2457