Braskem ML2400N LLDPE Injection Molding Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Molded
Manufacturer Braskem
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem ML2400N LLDPE Injection Molding Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The resin ML2400N is a linear low-density polyethylene, 1-butene based, with good flexibility and low warpage. It does not contain a slip agent. It does have narrow molecular weight distribution. This resin is used to produce masterbatches and injection molding of pigmented closures and houseware. This resin was developed to be injected under conditions comparable to polyethylene resins with a similar melt index and density range. Spiral flow: 29.6. Temperature Range: 150 to 210 ºC.
Physical Properties Metric English Comments
Density 0.926 g/cc
0.0335 lb/in³
ASTM-D1505
ESCR 10% Igepal® 1.5 hour

@Thickness 2.00 mm,
Temperature 50.0 °C
1.5 hour

@Thickness 0.0787 in,
Temperature 122 °F
0.3 mm notched-plaques; ASTM-D1693
Melt Flow 20 g/10 min

@Load 2.16 kg,
Temperature 190 °C
20 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM-D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 49
49
ASTM-D2240
Tensile Strength at Break 11.0 MPa
1600 psi
ASTM-D638
Tensile Strength, Yield 12.0 MPa
1740 psi
ASTM-D638
Elongation at Break 340 %
340 %
ASTM-D638
Elongation at Yield 16 %
16 %
ASTM-D882
Flexural Modulus, 1% Secant 415 MPa
60200 psi
ASTM-D790
Izod Impact, Notched 4.85 J/cm
9.09 ft-lb/in
ASTM-D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 46.0 °C
115 °F
ASTM-D648
Vicat Softening Point 94.0 °C

@Load 1.02 kg
201 °F

@Load 2.25 lb
ASTM-D1525