Braskem PB 608 LDPE Injection Molding Polyethylene

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Molded
Manufacturer	Braskem
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Braskem PB 608 LDPE Injection Molding Polyethylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: PB608 is a grade produced under high pressure in an autoclave reactor. This grade is especially designed for injection molding of articles that must show excellent flexibility properties and very good flow ability.Applications: Covers and parts with large flat area; injection molding. Information provided by Braskem

Physical Properties	Metric	English	Comments
Density	0.915 g/cc	0.0331 lb/in³	ASTM D1505
ESCR 100% Igepal®	15 hour @Thickness 3.00 mm, Temperature 23.0 °C	15 hour @Thickness 0.118 in, Temperature 73.4 °F	compression molded plaques; ASTM D1693
Melt Flow	30 g/10 min @Load 2.16 kg, Temperature 230 °C	30 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	39	39	ASTM D2240
Tensile Strength at Break	8.00 MPa	1160 psi	ASTM D638
Tensile Strength, Yield	8.00 MPa	1160 psi	ASTM D638
Elongation at Break	390 %	390 %	ASTM D638
Flexural Modulus, 1% Secant	450 MPa	65300 psi	ASTM D790

Thermal Properties	Metric	English	Comments
Vicat Softening Point	79.0 °C	174 °F	ASTM D1525

Processing Properties	Metric	English	Comments
Processing Temperature	180 - 210 °C	356 - 410 °F	Temperature profile
Mold Temperature	5.00 - 25.0 °C	41.0 - 77.0 °F