Bulk Molding Compounds BMC 610 - SP Mineral Filled, Glass Reinforced Polyester Compound, with UV Stabilizer

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Polyester, TS , Thermoset Polyester Glass and Mineral Filled BMC
Manufacturer BMC - Bulk Molding Compounds Inc.
Trade Name BMC
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Bulk Molding Compounds BMC 610 - SP Mineral Filled, Glass Reinforced Polyester Compound, with UV Stabilizer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BMC 610 molding compound is a mineral filled, glass fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is set a part form other medium impact electrical grade materials by its very high arc resistance and outstanding flame resistance in thin sections. BMC 610 comes in special colors for research products with UV stabilizerTypical applications include transformer bobbins, terminal boards, arc chutes and contactors.
Physical Properties Metric English Comments
Specific Gravity 1.88 - 1.92 g/cc
1.88 - 1.92 g/cc
Water Absorption 0.10 %
0.10 %
24 hours, 23°C
Linear Mold Shrinkage 0.0025 - 0.0045 cm/cm
0.0025 - 0.0045 in/in
Mechanical Properties Metric English Comments
Hardness, Barcol 30 - 40
30 - 40
Tensile Strength, Ultimate 41.4 - 55.2 MPa
6000 - 8000 psi
Flexural Strength 96.5 - 124 MPa
14000 - 18000 psi
Compressive Strength 165 - 193 MPa
24000 - 28000 psi
Izod Impact, Notched 1.07 - 2.14 J/cm
2.00 - 4.00 ft-lb/in
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) >= 260 °C
>= 500 °F
Flammability, UL94 V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0590 in
V-0

@Thickness 1.09 mm
V-0

@Thickness 0.0430 in
Electrical Properties Metric English Comments
Dielectric Constant 5.5

@Frequency 60 Hz
5.5

@Frequency 60 Hz
Dielectric Strength 14.2 kV/mm
360 kV/in
Short Time
Dissipation Factor 0.015

@Frequency 60 Hz
0.015

@Frequency 60 Hz
Arc Resistance >= 210 sec
>= 210 sec
Track Resistance >= 5400 sec
>= 5400 sec
Inclined Plane, 2.5kV
Comparative Tracking Index >= 600 V
>= 600 V
Processing Properties Metric English Comments
Mold Temperature 138 - 166 °C
280 - 330 °F