Bulk Molding Compounds BMC HT12-1027 Unsaturated Polyester Bulk Molding Compound

Category Polymer , Thermoset , Polyester, TS , Polyester (Thermoset) - Rigid
Manufacturer BMC - Bulk Molding Compounds Inc.
Trade Name BMC
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Bulk Molding Compounds BMC HT12-1027 Unsaturated Polyester Bulk Molding Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BMC HT12-1027 is a highly engineered Unsaturated Polyester Bulk Molding Compound developed for automotive under-hood applications. This compound is specified by Ford motor company for solenoid caps. Due to its excellent heat resistance and dimensional stability it performs well in automotive applications.Information provided by Bulk Molding Compounds, Inc.
Physical Properties Metric English Comments
Density 1.76 - 1.96 g/cc
0.0636 - 0.0708 lb/in³
Molded
Linear Mold Shrinkage 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
Mechanical Properties Metric English Comments
Hardness, Barcol 30 - 35
30 - 35
Tensile Strength 54.5 - 68.3 MPa
7900 - 9900 psi
Flexural Strength 164 - 192 MPa
23800 - 27800 psi
Flexural Modulus 12.4 - 13.8 GPa
1800 - 2000 ksi
Compressive Strength 170 - 198 MPa
24700 - 28700 psi
Izod Impact, Notched 8.01 - 9.08 J/cm
15.0 - 17.0 ft-lb/in
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 218 - 260 °C
425 - 500 °F
Flammability, UL94 HB
HB
This product is not currently UL listed.
Electrical Properties Metric English Comments
Dielectric Strength 14.4 - 16.4 kV/mm
367 - 417 kV/in
short time
Arc Resistance 182 sec
182 sec
Processing Properties Metric English Comments
Processing Temperature 143 - 171 °C
290 - 340 °F