Bulk Molding Compounds BMC T60-6009 Compression Grade Wear Resistant Molding Compound

Category Polymer , Thermoset , Polyester, TS , Polyester (Thermoset) - Rigid
Manufacturer BMC - Bulk Molding Compounds Inc.
Trade Name BMC
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Bulk Molding Compounds BMC T60-6009 Compression Grade Wear Resistant Molding Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BMC T60-6009 is a compression grade wear resistant molding compound. This material was specifically formulated for applications that require excellent abrasion resistance. Due to its low specific gravity it has substantial cost per cubic inch savings. BMC T60-6009 is UL listed and is typically used in power distribution equipment, switching components/relays, constant use switch applications and circuit protection breakers.Information provided by Bulk Molding Compounds, Inc.
Physical Properties Metric English Comments
Density 1.52 - 1.72 g/cc
0.0549 - 0.0621 lb/in³
Molded
Linear Mold Shrinkage 0.0030 - 0.0040 cm/cm
0.0030 - 0.0040 in/in
Mechanical Properties Metric English Comments
Hardness, Barcol 5.0 - 10
5.0 - 10
Tensile Strength 31.0 - 44.8 MPa
4500 - 6500 psi
Flexural Strength 58.6 - 86.2 MPa
8500 - 12500 psi
Flexural Modulus 3.79 - 5.17 GPa
550 - 750 ksi
Compressive Strength 95.1 - 123 MPa
13800 - 17800 psi
Izod Impact, Notched 1.60 - 2.67 J/cm
3.00 - 5.00 ft-lb/in
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) >= 260 °C
>= 500 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Dielectric Strength 13.2 - 15.2 kV/mm
335 - 385 kV/in
short time
Arc Resistance >= 190 sec
>= 190 sec
Comparative Tracking Index >= 500 V
>= 500 V
Processing Properties Metric English Comments
Processing Temperature 138 - 166 °C
280 - 330 °F