CP-Polymer-Technik Wellamid® 6600 HWS Nylon 66, Finely Crystalline, Heat Stabilized, Dry

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer CP-Polymer-Technik GmbH & Co.
Trade Name Wellamid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF CP-Polymer-Technik Wellamid® 6600 HWS Nylon 66, Finely Crystalline, Heat Stabilized, Dry.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by CP-Polymer-Technik GmbH & Co. KG
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 2.5 - 3.0 %
2.5 - 3.0 %
23°C/50%RH; DIN 53495
Linear Mold Shrinkage 0.0080 - 0.012 cm/cm

@Thickness 4.00 mm
0.0080 - 0.012 in/in

@Thickness 0.157 in
Mechanical Properties Metric English Comments
Tensile Strength, Yield 90.0 MPa
13100 psi
50 mm/min; ISO 527
Elongation at Break 10 %
10 %
50 mm/min; ISO 527
Elongation at Yield 4.0 %
4.0 %
50 mm/min; ISO 527
Tensile Modulus 3.40 GPa
493 ksi
ISO 527
Flexural Modulus 3.20 GPa
464 ksi
DIN 52457
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 0.600 J/cm²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear 85.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
47.2 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 53752
Melting Point 255 °C
491 °F
Kofler
Deflection Temperature at 0.46 MPa (66 psi) 200 °C
392 °F
ISO 179
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
ISO 179
Vicat Softening Point 230 °C
446 °F
50 N; ISO 306
Flammability, UL94 V-2

@Thickness 1.60 mm
V-2

@Thickness 0.0630 in
Stufe; IEC 707
V-2

@Thickness 3.20 mm
V-2

@Thickness 0.126 in
Stufe; IEC 707
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 93
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
ISO 3915
Dielectric Constant 3.4

@Frequency 1e+6 Hz
3.4

@Frequency 1e+6 Hz
IEC 250
Dielectric Strength 30.0 kV/mm
762 kV/in
IEC 243-1
Dielectric Loss Index 0.025
0.025
At 1 MHz; IEC 250
Comparative Tracking Index 600 V
600 V
Stufe; IEC 112
Processing Properties Metric English Comments
Melt Temperature 260 - 290 °C
500 - 554 °F
Mold Temperature 50.0 - 90.0 °C
122 - 194 °F
Descriptive Properties Value Comments
Back Pressure Low
Holding Pressure High
Injection Speed Medium to High
Screw Speed High