CP-Polymer-Technik Wellamid® 6600/58 GV 30 HWCP 30% Glass Fiber Nylon 66, Impact Modified Until -40°C, Heat Stabilized, Conditioned

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Reinforced, Impact Grade
Manufacturer CP-Polymer-Technik GmbH & Co.
Trade Name Wellamid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF CP-Polymer-Technik Wellamid® 6600/58 GV 30 HWCP 30% Glass Fiber Nylon 66, Impact Modified Until -40°C, Heat Stabilized, Conditioned.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by CP-Polymer-Technik GmbH & Co. KG
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 1.8 - 2.3 %
1.8 - 2.3 %
23°C/50%RH, Starting when dry; DIN 53495
Linear Mold Shrinkage 0.0020 cm/cm

@Thickness 4.00 mm
0.0020 in/in

@Thickness 0.157 in
Linear Mold Shrinkage, Transverse 0.0070 cm/cm

@Thickness 4.00 mm
0.0070 in/in

@Thickness 0.157 in
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa
13100 psi
5 mm/min; ISO 527
Elongation at Break 6.0 %
6.0 %
5 mm/min; ISO 527
Tensile Modulus 5.00 GPa
725 ksi
ISO 527
Charpy Impact Unnotched 10.5 J/cm²

@Temperature 23.0 °C
50.0 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 3.60 J/cm²

@Temperature 23.0 °C
17.1 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
Melting Point 255 °C
491 °F
Kofler
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
IEC 93
Surface Resistance 1.00e+10 ohm
1.00e+10 ohm
ISO 3915
Dielectric Constant 6.0

@Frequency 1e+6 Hz
6.0

@Frequency 1e+6 Hz
IEC 250
Dielectric Strength 35.0 kV/mm
889 kV/in
IEC 243-1
Dielectric Loss Index 0.15
0.15
At 1 MHz; IEC 250
Processing Properties Metric English Comments
Melt Temperature 265 - 295 °C
509 - 563 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Descriptive Properties Value Comments
Back Pressure Low
Holding Pressure High
Injection Speed High
Screw Speed Medium