CTC X-PRO TF 1113 HP Polypropylene Homopolymer, 13% Talc Filled

Category	Polymer , Renewable/Recycled Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler
Manufacturer	CTC (Composite Technologies)
Trade Name	X-PRO
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	CTC X-PRO TF 1113 HP Polypropylene Homopolymer, 13% Talc Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

X-PRO TF 1113 HP is a 13% talc reinforced polypropylene homopolymer, heat stabilized, and made of 98% recycled content. It has applications in: automotive under hood, IP components, fan and lighting shrouds, HVAC components, lawn & garden, pipe fittings, and appliances.Data provided by Composite Technologies (CTC).

Physical Properties	Metric	English	Comments
Melt Flow	20 g/10 min	20 g/10 min	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	30.0 MPa	4350 psi	ISO 527-1/2
Flexural Modulus	1.80 GPa	261 ksi	0.05 in/min; ISO 178
Izod Impact, Notched (ISO)	3.00 kJ/m²	1.43 ft-lb/in²	Low Temp; ISO 180/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	118 °C	245 °F	ASTM-D648
Deflection Temperature at 1.8 MPa (264 psi)	60.0 °C	140 °F	ASTM-D648

Processing Properties	Metric	English
Rear Barrel Temperature	204 - 216 °C	400 - 420 °F
Middle Barrel Temperature	216 - 227 °C	420 - 440 °F
Front Barrel Temperature	227 - 238 °C	440 - 460 °F
Melt Temperature	227 - 238 °C	440 - 460 °F
Mold Temperature	26.7 - 60.0 °C	80.0 - 140 °F
Back Pressure	0.689 - 1.03 MPa	100 - 150 psi
Clamp Pressure	27.6 - 34.5 MPa	4000 - 5000 psi

Descriptive Properties	Value	Comments
Boost Pressure (psi)	750-1500
Hold Pressure	50 - 75% of Boost
Screw Speed	Fast