Calsak CS-72 General Purpose ABS Resin

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
Manufacturer Calsak
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Calsak CS-72 General Purpose ABS Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Characteristics:High Impact, High GlossInjection molding grade
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Melt Flow 5.0 g/10 min

@Load 3.80 kg,
Temperature 230 °C
5.0 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 109
109
ASTM D785
Tensile Strength, Yield 42.1 MPa

@Thickness 3.17 mm
6100 psi

@Thickness 0.125 in
Type I; ASTM D638
Elongation at Break 30 %
30 %
ASTM D638
Tensile Modulus 2.55 GPa

@Thickness 3.17 mm
370 ksi

@Thickness 0.125 in
Type I; ASTM D638
Flexural Strength 72.4 MPa

@Thickness 3.17 mm
10500 psi

@Thickness 0.125 in
ASTM D790
Flexural Modulus 2.62 GPa

@Thickness 3.17 mm
380 ksi

@Thickness 0.125 in
ASTM D790
Izod Impact, Notched 3.74 J/cm

@Thickness 3.17 mm
7.00 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C

@Thickness 3.17 mm
185 °F

@Thickness 0.125 in
Unannealed; ASTM D648
94.4 °C

@Thickness 3.17 mm
202 °F

@Thickness 0.125 in
Annealed; ASTM D648
Vicat Softening Point 106 °C
223 °F
ASTM D1525
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0625 in
Processing Properties Metric English Comments
Rear Barrel Temperature 235 - 249 °C
455 - 480 °F
Middle Barrel Temperature 241 - 254 °C
465 - 490 °F
Front Barrel Temperature 246 - 260 °C
475 - 500 °F
Nozzle Temperature 246 - 260 °C
475 - 500 °F
Melt Temperature 246 - 302 °C
475 - 575 °F
Mold Temperature 43.3 - 65.6 °C
110 - 150 °F
Drying Temperature 82.2 - 87.8 °C

@Time 7200 sec
180 - 190 °F

@Time 2.00 hour
Injection Pressure 68.9 - 110 MPa
10000 - 16000 psi
Back Pressure 0.000 - 0.172 MPa
0.000 - 25.0 psi
Clamp Pressure 13.8 - 27.6 MPa
2000 - 4000 psi
Descriptive Properties Value Comments
Hold Pressure 50 - 75% of injection pressure
Injection Speed High
Screw Speed Moderate