Carpenter AerMet® 100 Aged at 875°F
| Category | Metal , Ferrous Metal , Alloy Steel , Tool Steel |
| Manufacturer | Carpenter Technology Corporation (Cartech) |
| Trade Name | AerMet® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Carpenter AerMet® 100 Aged at 875°F.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
An alloy providing high hardness and strength combined with exceptional ductility and toughness. This alloy should be considered for aircraft and aerospace structural components requiring high strength, high fracture toughness and exceptional stress corrosion cracking resistance. AerMet 100 may be considered for use up to about 800°F (427°C). This alloy is not subject to the same restrictions as AF1410, thus may be considered a substitute.UNS K92580
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.89 g/cc | 0.285 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 2080 MPa | 302000 psi | |
| Tensile Strength, Yield | 1780 MPa | 258000 psi | |
| Elongation at Break | 14.2 % | 14.2 % | |
| Reduction of Area | 63.8 % | 63.8 % | |
| Tensile Modulus | 192 GPa | 27900 ksi | |
| Fatigue Strength | 945 MPa @# of Cycles 1.00e+7 |
137000 psi @# of Cycles 1.00e+7 |
R=-1, Kt=1 |
| Fracture Toughness | 108.5 MPa-m½ | 98.70 ksi-in½ | |
| Charpy Impact | 40.7 J | 30.0 ft-lb | notched |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.23 % | 0.23 % | |
| Chromium, Cr | 3.1 % | 3.1 % | |
| Cobalt, Co | 13.4 % | 13.4 % | |
| Iron, Fe | 70.97 % | 70.97 % | |
| Molybdenum, Mo | 1.2 % | 1.2 % | |
| Nickel, Ni | 11.1 % | 11.1 % |