Celanese Ateva® 1062 Ethylene Vinyl Acetate Copolymer Film  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Extrusion/Coating Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Ateva® 1062 Ethylene Vinyl Acetate Copolymer Film  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Laminating and coextrusion; excellent sealability, opticals, strength, and antiblocking characteristics.
Physical Properties Metric English Comments
Density 0.926 g/cc
0.0335 lb/in³
ASTM D1505
Vinyl Acetate Content 6.0 %
6.0 %
Melt Flow 1.8 g/10 min
1.8 g/10 min
ASTM D1238 Cond. E
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 9.00 MPa
1310 psi
ASTM D882
Film Tensile Strength at Yield, TD 9.00 MPa
1310 psi
ASTM D882
Film Elongation at Break, MD 360 %
360 %
ASTM D882
Film Elongation at Break, TD 500 %
500 %
ASTM D882
Secant Modulus, MD 0.120 GPa
17.4 ksi
ASTM D882
Secant Modulus, TD 0.125 GPa
18.1 ksi
ASTM D882
Coefficient of Friction 0.75
0.75
ASTM D1894
Dart Drop Test 90.0 g
0.198 lb
Thickness not specified @ 50% Fail, ASTM D1709
Film Tensile Strength at Break, MD 23.0 MPa
3340 psi
ASTM D882
Film Tensile Strength at Break, TD 16.0 MPa
2320 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 104 °C
219 °F
ASTM D3417
Optical Properties Metric English Comments
Haze 7.0 %
7.0 %
ASTM D2457
Gloss 64 %
64 %
45° Gloss, ASTM D2457
Processing Properties Metric English Comments
Processing Temperature 160 - 210 °C
320 - 410 °F