Celanese Celanex® 2002-2 PBT  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer
Trade Name Celanex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Celanex® 2002-2 PBT  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Celanex 2002-2 is a general purpose, unreinforced polybutylene terephthalate with a good balance of mechanical properties and processability. Celanex 2002-2 ia a medium flow material that contains an internal lubricant.Medium melt flow, lubricatedInformation provided by Celanese
Physical Properties Metric English Comments
Specific Gravity 1.31 g/cc
1.31 g/cc
ASTM D792
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Water Absorption 0.090 %
0.090 %
24hr immersion; ASTM D570
Linear Mold Shrinkage, Flow 0.018 - 0.020 cm/cm
0.018 - 0.020 in/in
ASTM D955
0.018 - 0.020 cm/cm
0.018 - 0.020 in/in
ISO 294-4
Melt Flow 20 g/10 min
20 g/10 min
ASTM D1238
20 g/10 min

@Load 2.16 kg,
Temperature 250 °C
20 g/10 min

@Load 4.76 lb,
Temperature 482 °F
(MVR) cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 78
78
ISO 2039-2
Tensile Strength at Break 55.8 MPa
8100 psi
ASTM D638
60.0 MPa
8700 psi
50mm/min; ISO 527-2/1A
Tensile Stress 30.0 MPa

@Strain 50.0 %
4350 psi

@Strain 50.0 %
50mm/min; ISO 527-2/1A
Tensile Strength, Yield 55.8 MPa
8100 psi
ASTM D638
60.0 MPa
8700 psi
50mm/min; ISO 527-2/1A
17.9 MPa

@Temperature 121 °C
2600 psi

@Temperature 250 °F
ASTM D638
24.8 MPa

@Temperature 80.0 °C
3600 psi

@Temperature 176 °F
ASTM D638
75.8 MPa

@Temperature 0.000 °C
11000 psi

@Temperature 32.0 °F
ASTM D638
101 MPa

@Temperature -40.0 °C
14600 psi

@Temperature -40.0 °F
ASTM D638
Elongation at Break >= 50 %
>= 50 %
50mm/min; ISO 527-2/1A
200 %

@Temperature 22.8 °C
200 %

@Temperature 73.0 °F
ASTM D638
Elongation at Yield 4.0 %
4.0 %
50mm/min; ISO 527-2/1A
3.2 %

@Temperature 22.8 °C
3.2 %

@Temperature 73.0 °F
ASTM D638
4.4 %

@Temperature 0.000 °C
4.4 %

@Temperature 32.0 °F
ASTM D638
7.2 %

@Temperature -40.0 °C
7.2 %

@Temperature -40.0 °F
ASTM D638
17 %

@Temperature 80.0 °C
17 %

@Temperature 176 °F
ASTM D638
23 %

@Temperature 121 °C
23 %

@Temperature 250 °F
ASTM D638
Tensile Modulus 2.60 GPa
377 ksi
1mm/min; ISO 527-2/1A
0.296 GPa

@Temperature 121 °C
43.0 ksi

@Temperature 250 °F
ASTM D638
0.469 GPa

@Temperature 176 °C
68.0 ksi

@Temperature 349 °F
ASTM D638
3.10 GPa

@Temperature -40.0 °C
450 ksi

@Temperature -40.0 °F
ASTM D638
3.17 GPa

@Temperature 22.8 °C
460 ksi

@Temperature 73.0 °F
ASTM D638
Flexural Strength 80.0 MPa
11600 psi
ISO 178
86.2 MPa
12500 psi
ASTM D790
Flexural Modulus 2.50 GPa
363 ksi
ISO 178
2.55 GPa

@Temperature 22.8 °C
370 ksi

@Temperature 73.0 °F
ASTM D790
Izod Impact, Notched 0.481 J/cm
0.900 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched NB
NB
ISO 179/1eU
19.0 J/cm²

@Temperature -30.0 °C
90.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
ISO 179/1eA
0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 110 µm/m-°C
61.1 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 127 µm/m-°C
70.6 µin/in-°F
ISO 11359-2
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1,-2,-3
225 °C
437 °F
ASTM D3418
Transformation Temperature, Tg 60.0 °C
140 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 0.46 MPa (66 psi) 150 °C
302 °F
ISO 75-1, -2
160 °C
320 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
ASTM D648
55.0 °C
131 °F
ISO 75-1, -2
Vicat Softening Point 190 °C
374 °F
B50 (50°C/h 50N); ISO 306
Flammability, UL94 HB
HB
UL94
HB

@Thickness 0.710 mm
HB

@Thickness 0.0280 in
UL94
Oxygen Index 22 %
22 %
ISO 4589
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
3.2

@Frequency 1.00e+6 Hz
ASTM D150
3.5

@Frequency 1.00e+6 Hz
3.5

@Frequency 1.00e+6 Hz
IEC 60250
4.0

@Frequency 100 Hz
4.0

@Frequency 100 Hz
IEC 60250
Dielectric Strength 16.5 kV/mm
420 kV/in
short term; ASTM D149
23.0 kV/mm
584 kV/in
IEC 60243-1
Dissipation Factor 0.0014

@Frequency 100 Hz
0.0014

@Frequency 100 Hz
IEC 60250
0.022

@Frequency 1.00e+6 Hz
0.022

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature 20.0 - 50.0 °C
68.0 - 122 °F
65.0 - 93.0 °C
149 - 199 °F
Cavity temperature
Feed Temperature 230 - 240 °C
446 - 464 °F
Rear Barrel Temperature 230 - 240 °C
446 - 464 °F
Middle Barrel Temperature 235 - 250 °C
455 - 482 °F
Front Barrel Temperature 240 - 260 °C
464 - 500 °F