Celanese Celstran® PP-GF50-0455 P10/10 PP, 50% Glass Reinforced

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 50% Glass Fiber Filler
Manufacturer Celanese Corporation
Trade Name CELSTRAN
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese Celstran® PP-GF50-0455 P10/10 PP, 50% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Material code according to ISO 1043-1: PPInformation provided by Celanese
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Tensile Strength at Break 140 MPa
20300 psi
5mm/min; ISO 527-2/1A
Tensile Strength 85.0 MPa

@Temperature 80.0 °C
12300 psi

@Temperature 176 °F
ISO 527-1, -2
Elongation at Break 1.20 %
1.20 %
5mm/min; ISO 527-2/1A
2.30 %

@Temperature 80.0 °C
2.30 %

@Temperature 176 °F
ISO 527-1, -2
Tensile Modulus 11.5 GPa
1670 ksi
50mm/min; ISO 527-2/1A
8.40 GPa

@Temperature 80.0 °C
1220 ksi

@Temperature 176 °F
ISO 527-1, -2
Flexural Strength 210 MPa
30500 psi
ISO 178
120 MPa

@Temperature 80.0 °C
17400 psi

@Temperature 176 °F
ISO 178
Flexural Modulus 12.0 GPa
1740 ksi
ISO 178
8.20 GPa

@Temperature 80.0 °C
1190 ksi

@Temperature 176 °F
ISO 178
Charpy Impact Unnotched 5.50 J/cm²
26.2 ft-lb/in²
ISO 179/1eU
5.20 J/cm²

@Temperature -30.0 °C
24.7 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 2.80 J/cm²
13.3 ft-lb/in²
ISO 179/1eA
3.50 J/cm²

@Temperature -30.0 °C
16.7 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 165 °C
329 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi) 158 °C
316 °F
ISO 75-1, -2
Deflection Temperature at 8.0 MPa 138 °C
280 °F
ISO 75-1, -2
Processing Properties Metric English Comments
Processing Temperature 40.0 - 70.0 °C
104 - 158 °F
cavity
260 - 290 °C
500 - 554 °F
hot runner
Feed Temperature 20.0 - 50.0 °C
68.0 - 122 °F
Zone 1 250 - 260 °C
482 - 500 °F
Zone 2 260 - 270 °C
500 - 518 °F
Zone 3 270 - 280 °C
518 - 536 °F
Zone 4 280 - 290 °C
536 - 554 °F
Die Temperature 280 - 290 °C
536 - 554 °F
Melt Temperature 260 - 290 °C
500 - 554 °F
Drying Temperature 90.0 - 100 °C
194 - 212 °F
Dry Time 2.00 hour
2.00 hour
Moisture Content <= 0.200 %
<= 0.200 %
Injection Pressure 60.0 - 120 MPa
8700 - 17400 psi
Hold Pressure 40.0 - 80.0 MPa
5800 - 11600 psi
Back Pressure <= 3.00 MPa
<= 435 psi
Screw Speed 25.0 rpm

@Diameter 75.0 mm
25.0 rpm

@Diameter 2.95 in
35.0 rpm

@Diameter 55.0 mm
35.0 rpm

@Diameter 2.17 in
50.0 rpm

@Diameter 40.0 mm
50.0 rpm

@Diameter 1.57 in
Descriptive Properties Value Comments
Heat stabilized/stable to heat Yes
Injection molding Yes
Injection Speed slow
Light stabilized/stable to light Yes
Sheet extrusion Yes
UV stabilized/stable to weather Yes