Celanese FORTRON 6345L4 PPS, 30% Specialty

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler
Manufacturer Celanese Corporation
Trade Name FORTRON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese FORTRON 6345L4 PPS, 30% Specialty.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Fortron 6345L4 is 30% glass fiber/high PTFE reinforced injection molding grade. This grade, available in natural and black color, exhibits improved wear and sliding properties versus 1342L4 product.Information provided by Celanese
Physical Properties Metric English Comments
Density 1.66 g/cc
0.0600 lb/in³
ISO 1183
Moisture Absorption 0.0200 %
0.0200 %
23°C/50%RH; ISO 62
Linear Mold Shrinkage, Flow 0.00300 - 0.00500 cm/cm
0.00300 - 0.00500 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.00600 - 0.00900 cm/cm
0.00600 - 0.00900 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 150 MPa
21800 psi
5mm/min; ISO 527-2/1A
Elongation at Break 1.90 %
1.90 %
5mm/min; ISO 527-2/1A
Flexural Strength 230 MPa
33400 psi
ISO 178
Flexural Modulus 10.6 GPa
1540 ksi
ISO 178
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
ISO 180/1A
Coefficient of Friction, Dynamic 0.150
0.150
steel; ASTM D1894
0.280
0.280
fortron; ASTM D1894
Coefficient of Friction, Static 0.170
0.170
steel; ASTM D1894
0.290
0.290
fortron; ASTM D1894
K (wear) Factor 242 x 10-8 mm³/N-M
120 x 10-10 in³-min/ft-lb-hr
C-1018 steel,16 µ-in,120F,PV2000,40 psi,50 ft/min; ASTM D3702
298 x 10-8 mm³/N-M
148 x 10-10 in³-min/ft-lb-hr
416 Stainless,16 µ-in,90F,PV2000,40 psi,50 ft/min; ASTM D3702
836 x 10-8 mm³/N-M
415 x 10-10 in³-min/ft-lb-hr
C-1018 steel,16 µ-in,200F,PV2000,40 psi,50 ft/min; ASTM D3702
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 260 °C
500 °F
ISO 75-1, -2
Deflection Temperature at 8.0 MPa 190 °C
374 °F
ISO 75-1, -2
Processing Properties Metric English Comments
Processing Temperature 140 - 160 °C
284 - 320 °F
cavity
330 - 340 °C
626 - 644 °F
hot runner
Feed Temperature 60.0 - 80.0 °C
140 - 176 °F
Middle Barrel Temperature 20.0 - 30.0 °C
68.0 - 86.0 °F
Zone 1 290 - 300 °C
554 - 572 °F
Zone 2 310 - 320 °C
590 - 608 °F
Zone 3 330 - 340 °C
626 - 644 °F
Zone 4 330 - 340 °C
626 - 644 °F
Die Temperature 310 - 330 °C
590 - 626 °F
Melt Temperature 330 - 340 °C
626 - 644 °F
Drying Temperature 130 - 140 °C
266 - 284 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Moisture Content <= 0.0200 %
<= 0.0200 %
Injection Pressure 50.0 - 100 MPa
7250 - 14500 psi
Hold Pressure 30.0 - 70.0 MPa
4350 - 10200 psi
Back Pressure <= 3.00 MPa
<= 435 psi
Screw Speed 50.0 rpm

@Diameter 55.0 mm
50.0 rpm

@Diameter 2.17 in
75.0 rpm

@Diameter 40.0 mm
75.0 rpm

@Diameter 1.57 in
120 rpm

@Diameter 25.0 mm
120 rpm

@Diameter 0.984 in
Descriptive Properties Value Comments
Injection Speed fast