Celanese FORTRON® 9140L6 40% Glass Reinforced Polyphenylene Sulfide (PPS)

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler
Manufacturer Celanese Corporation
Trade Name Fortron®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese FORTRON® 9140L6 40% Glass Reinforced Polyphenylene Sulfide (PPS).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Fortron 9140L6 is a 40% glass fiber reinforced injection molding grade with a low melt viscosity. It exhibits excellent heat and chemical resistance, inherent flame retardancy and shows high hardness and rigidity at elevated temperatures. 9140L6 is used for thin walled parts with long flow lengths. Components made of this grade may be used for medical, dental, pharmaceutical, and certain food handling applications. Fortron 9140L6 is in compliance with ISO 10993, USP Class VI, and is included in the Fortron Drug and Device Master Files at the FDA. It complies with the FDA Food Contact Notification (FCN-No. 40) for repeat-use applications.Information provided by Celanese Corporation.
Physical Properties Metric English Comments
Density 1.65 g/cc
0.0596 lb/in³
ISO 1183
Water Absorption at Saturation 0.020 %
0.020 %
ISO 62
Linear Mold Shrinkage 0.0020 - 0.0060 cm/cm
0.0020 - 0.0060 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 100
100
ISO 2039-2
Tensile Strength at Break 190 MPa
27600 psi
5 mm/min; ISO 527-2/1A
Elongation at Break 1.8 %
1.8 %
5 mm/min; ISO 527-2/1A
Flexural Strength 280 MPa
40600 psi
ISO 178
Flexural Modulus 14.0 GPa
2030 ksi
ISO 178
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
ISO 180/1A
Izod Impact, Unnotched (ISO) 32.0 kJ/m²
15.2 ft-lb/in²
ISO 180/1U
Charpy Impact Unnotched 4.80 J/cm²
22.8 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 280 °C
536 °F
ISO 11357-1,2,3
Deflection Temperature at 1.8 MPa (264 psi) 270 °C
518 °F
ISO 75-1, -2
Deflection Temperature at 8.0 MPa 200 °C
392 °F
ISO 75-1, -2
Glass Transition Temp, Tg 90.0 °C
194 °F
ISO 11357-1,-2,-3
Processing Properties Metric English Comments
Melt Temperature 310 - 340 °C
590 - 644 °F
Mold Temperature 135 - 160 °C
275 - 320 °F
Drying Temperature 135 °C
275 °F
Dry Time 3 - 4 hour
3 - 4 hour