Celanese VECTRA MT1310 LCP, 30% Medical Technology

Category Polymer , Thermoplastic , Liquid Crystal Polymer (LCP) , Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled
Manufacturer Celanese Corporation
Trade Name VECTRA
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Celanese VECTRA MT1310 LCP, 30% Medical Technology.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Standard for the Industry. Excellent balance of properties, including easy flow, easy processing, thermal stability, chemical resistance, mechanical and electrical properties. Suitable for vapor phase surface mount electrical and electronic devices. 30% glass reinforcedInformation provided by Celanese
Physical Properties Metric English Comments
Density 1.62 g/cc
0.0585 lb/in³
ISO 1183
Moisture Absorption 0.0400 %
0.0400 %
23°C/50%RH; ISO 62
Linear Mold Shrinkage, Flow 0.00200 cm/cm
0.00200 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.00400 cm/cm
0.00400 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 85.0
85.0
ISO 2039-2
Tensile Strength at Break 190 MPa
27600 psi
5mm/min; ISO 527-2/1A
Elongation at Break 2.10 %
2.10 %
5mm/min; ISO 527-2/1A
Tensile Modulus 15.0 GPa
2180 ksi
50mm/min; ISO 527-2/1A
Flexural Strength 280 MPa
40600 psi
ISO 178
Flexural Modulus 14.5 GPa
2100 ksi
ISO 178
Compressive Strength 100 MPa

@Strain 1.00 %
14500 psi

@Strain 1.00 %
ISO 604
Compressive Modulus 14.5 GPa
2100 ksi
ISO 604
Izod Impact, Notched (ISO) 24.0 kJ/m²
11.4 ft-lb/in²
ISO 180/1A
29.0 kJ/m²

@Temperature 23.0 °C
13.8 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched 3.30 J/cm²
15.7 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 2.60 J/cm²
12.4 ft-lb/in²
ISO 179/1eA
Tensile Creep Modulus, 1 hour 12600 MPa
1.83e+6 psi
ISO 899-1
Tensile Creep Modulus, 1000 hours 10900 MPa
1.58e+6 psi
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 6.00 µm/m-°C
3.33 µin/in-°F
ISO 11359-2
CTE, linear, Transverse to Flow 23.0 µm/m-°C
12.8 µin/in-°F
ISO 11359-2
Melting Point 280 °C
536 °F
10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 235 °C
455 °F
ISO 75-1, -2
Deflection Temperature at 8.0 MPa 190 °C
374 °F
ISO 75-1, -2
Vicat Softening Point 160 °C
320 °F
ISO 306
Flammability, UL94 V-0
V-0
Oxygen Index 45.0 %
45.0 %
ISO 4589
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.70

@Frequency 1.00e+6 Hz
3.70

@Frequency 1.00e+6 Hz
IEC 60250
4.20

@Frequency 100 Hz
4.20

@Frequency 100 Hz
IEC 60250
Dielectric Strength 31.0 kV/mm
787 kV/in
IEC 60243-1
Dissipation Factor 0.0160

@Frequency 100 Hz
0.0160

@Frequency 100 Hz
IEC 60250
0.0180

@Frequency 1.00e+6 Hz
0.0180

@Frequency 1.00e+6 Hz
IEC 60250
Arc Resistance 140 sec
140 sec
Internal
Comparative Tracking Index 175 V
175 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature 80.0 - 120 °C
176 - 248 °F
cavity
285 - 295 °C
545 - 563 °F
hot runner
Feed Temperature 60.0 - 80.0 °C
140 - 176 °F
Middle Barrel Temperature 20.0 - 30.0 °C
68.0 - 86.0 °F
Zone 1 270 - 280 °C
518 - 536 °F
Zone 2 275 - 285 °C
527 - 545 °F
Zone 3 280 - 290 °C
536 - 554 °F
Zone 4 285 - 295 °C
545 - 563 °F
Die Temperature 290 - 300 °C
554 - 572 °F
Melt Temperature 285 - 295 °C
545 - 563 °F
293 °C
559 °F
ISO 294
Mold Temperature 60.0 °C
140 °F
ISO 294
Injection Velocity 150 mm/sec
5.91 in/sec
ISO 294
Drying Temperature >= 150 °C
>= 302 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Moisture Content <= 0.0100 %
<= 0.0100 %
Injection Pressure 50.0 - 150 MPa
7250 - 21800 psi
Hold Pressure 48.0 MPa
6960 psi
ISO 294
50.0 - 150 MPa
7250 - 21800 psi
Back Pressure <= 3.00 MPa
<= 435 psi
Screw Speed 80.0 rpm

@Diameter 40.0 mm
80.0 rpm

@Diameter 1.57 in
140 rpm

@Diameter 25.0 mm
140 rpm

@Diameter 0.984 in
200 rpm

@Diameter 16.0 mm
200 rpm

@Diameter 0.630 in
Descriptive Properties Value Comments
Injection molding Yes
Injection Speed very fast