Chang Chun Plastic Longlite PM T357 Electrical Phenolic Molding Compound

Category Polymer , Thermoset , Phenolic , Phenolic; Unreinforced; Molded
Manufacturer Chang Chun Plastic Co. Ltd.
Trade Name Longlite PM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chang Chun Plastic Longlite PM T357 Electrical Phenolic Molding Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ASTM Grades per ASTM D700 are 2, 3.Information provided by Dowell Trading Company Ltd.
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ASTM D792
Water Absorption 0.30 %
0.30 %
ASTM D570
Linear Mold Shrinkage 0.0070 cm/cm
0.0070 in/in
Compression; ASTM D955
0.0090 cm/cm
0.0090 in/in
Transfer; ASTM D955
0.012 cm/cm
0.012 in/in
Injection; ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 55.0 MPa
7980 psi
ASTM D651
Flexural Yield Strength 88.0 MPa
12800 psi
ASTM D790
Compressive Yield Strength 207 MPa
30000 psi
ASTM D695
Izod Impact, Notched 0.290 J/cm
0.543 ft-lb/in
ASTM D256
Charpy Impact, Notched 0.340 J/cm²
1.62 ft-lb/in²
ASTM D256
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 180 °C
356 °F
Two Hour Heat Resistance per ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 170 °C
338 °F
ASTM D648
Flammability, UL94 V-0

@Thickness 0.790 mm
V-0

@Thickness 0.0311 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
ASTM D257
Insulation Resistance 1.00e+9 ohm
1.00e+9 ohm
After Boiling; ASTM D257
1.00e+11 ohm
1.00e+11 ohm
Normal; ASTM D257
Dielectric Strength 12.8 kV/mm
325 kV/in
ASTM D149
Arc Resistance 120 sec
120 sec
ASTM D495
Comparative Tracking Index 100 - 175 V
100 - 175 V
UL PLC 4