Chase Plastics CP Pryme® NN333L (Dry) Nylon 66, 33% Glass Fiber Reinforced, Lubricated, Recycled Content
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Chase Plastics |
| Trade Name | CP Pryme® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chase Plastics CP Pryme® NN333L (Dry) Nylon 66, 33% Glass Fiber Reinforced, Lubricated, Recycled Content.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: LubricatedRecycled ContentForm: PelletsInformation provided by Chase Plastics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| Filler Content | 33 % | 33 % | |
| Water Absorption | 0.70 % | 0.70 % | At 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | 0.125 in; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 99 | 99 | ASTM D785 |
| Tensile Strength at Break | 148 MPa | 21500 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Flexural Strength | 234 MPa | 34000 psi | ASTM D790 |
| Flexural Modulus | 8.27 GPa | 1200 ksi | ASTM D790 |
| Tensile Impact Strength | 2.94 kJ/m² | 1.40 ft-lb/in² | 0.125 in; ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 255 °C | 491 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | Unannealed; ASTM D648 |