Chesterton ARC S1 General purpose coating

Category Polymer , Thermoset , Epoxy
Manufacturer Chesterton
Trade Name ARC
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chesterton ARC S1 General purpose coating.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: An advanced polymer composite formulated to protect metal surfaces from corrosion and chmical attack. It is normally applied at a thickness of 250 microns (10 mils) per coat. Non-shrinking, 100% solids. ARC S1 is a low viscosity high performance composite lining that is designed to be spray applied but may also be applied by roller or brush. As a one coat system, it functions as a corrosion resistant primer for many high performance coatings. ARC S1 yields excellent barrier properties for long-term corrosion and chemical resistance in immersion exposures when used in a multicoat application. The cured ARC S1 provides a high gloss surface with adhesion and resistance to corrosion. Benefits:Outlasts conventional paints and coatingsLong pot life allows for ease of use100% solids, no shrinkage on cureOutstanding adhesion insures reliable performance against under film corrosionAble to be high voltage spark tested for pinhole free films Suggested Uses:Chemical Storage TanksStructural SteelPipeline CoatingsClarifier TanksPetroleum Storage TanksCooling Water SystemsService Water SystemThickener TanksInformation provided by Chesterton
Physical Properties Metric English Comments
Density 1.50 g/cc
0.0542 lb/in³
Cured
Mechanical Properties Metric English Comments
Hardness, Shore D 85
85
ASTM D2240
Tensile Strength at Break 23.4 MPa
3400 psi
ASTM D638
Elongation at Break 3.0 %
3.0 %
ASTM D638
Flexural Strength 41.4 MPa
6000 psi
ASTM D790
Flexural Modulus 1.93 GPa
280 ksi
ASTM D790
Adhesive Bond Strength >= 13.8 MPa
>= 2000 psi
ASTM D4541
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 52.0 °C
126 °F
Wet Service
80.0 °C
176 °F
Dry Service
Deflection Temperature at 0.46 MPa (66 psi) 46.0 °C
115 °F
ASTM D648
Processing Properties Metric English Comments
Cure Time 240 min

@Temperature 32.0 °C
4.00 hour

@Temperature 89.6 °F
Tack Free
360 min

@Temperature 25.0 °C
6.00 hour

@Temperature 77.0 °F
Tack Free
420 min

@Temperature 16.0 °C
7.00 hour

@Temperature 60.8 °F
Tack Free
480 min

@Temperature 10.0 °C
8.00 hour

@Temperature 50.0 °F
Tack Free
720 min

@Temperature 32.0 °C
12.0 hour

@Temperature 89.6 °F
Light Load
1080 min

@Temperature 25.0 °C
18.0 hour

@Temperature 77.0 °F
Light Load
1440 min

@Temperature 16.0 °C
24.0 hour

@Temperature 60.8 °F
Light Load
1440 min

@Temperature 32.0 °C
24.0 hour

@Temperature 89.6 °F
Overcoat End
1440 min

@Temperature 32.0 °C
24.0 hour

@Temperature 89.6 °F
Full Load
1800 min

@Temperature 25.0 °C
30.0 hour

@Temperature 77.0 °F
Overcoat End
2160 min

@Temperature 10.0 °C
36.0 hour

@Temperature 50.0 °F
Light Load
2160 min

@Temperature 16.0 °C
36.0 hour

@Temperature 60.8 °F
Overcoat End
2160 min

@Temperature 25.0 °C
36.0 hour

@Temperature 77.0 °F
Full Load
2640 min

@Temperature 10.0 °C
44.0 hour

@Temperature 50.0 °F
Overcoat End
2880 min

@Temperature 16.0 °C
48.0 hour

@Temperature 60.8 °F
Full Load
4320 min

@Temperature 10.0 °C
72.0 hour

@Temperature 50.0 °F
Full Load
7200 min

@Temperature 32.0 °C
120 hour

@Temperature 89.6 °F
Full Chemical
10100 min

@Temperature 25.0 °C
168 hour

@Temperature 77.0 °F
Full Chemical
12600 min

@Temperature 16.0 °C
210 hour

@Temperature 60.8 °F
Full Chemical
134000 min

@Temperature 10.0 °C
2240 hour

@Temperature 50.0 °F
Full Chemical
Descriptive Properties Value Comments
Color Blue