Chevron Phillips K-Resin® KR10 Styrene-Butadiene Copolymer, Film Grade  (discontinued **)

Category Polymer , Film , Thermoplastic , Styrene-Butadiene , Styrene-Butadiene Copolymer, SBC
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chevron Phillips K-Resin® KR10 Styrene-Butadiene Copolymer, Film Grade  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Styrene-Butadiene Copolymer. Properties below based on 1 mil ( 0.025 mm) film; 2.5:1 Blow Up Ratio; 35 mil (0.90 mm) die gap.Customer Benefits: This SBC is easily processed on blown film or cast film equipment to give tough, high clarity film. Film produced has excellent clarity, good toughness, excellent stiffness, good heat sealability, high surface gloss, and high permeation. Has a puncture value of 1.2 J as per ASTM D3763, a 99 % crease retention as per TAPPI T446-B, and a 0.6 g mm/m^2 24h moisture vapor transmission as per ASTM F1249 at 23°C. Film shrinkage is 67% MD and 48% TD.Applications: Major applications include medical packaging, produce packaging, skin packaging, twist wrap, lidstock film, labeling film, decorative films, industrial films, shrink wrap, overwrap film, barrier film, and tamper evident packagingProcessing Recommendations:Blown Film: Melt Temperature, 166-193°C recommended. Cast Film: Melt Temperature, 193-216°C recommended. High shear and restrictive type screws tend to degrade the melt.Specification Data: FDA Regulation 21 CFR 177.1640. Suitable for food contact. EEC Directive 90/128/EEC and all its amendments. USP Class VI-50. UL 94HB.Data provided by Chevron Phillips Chemical Company LP.
Physical Properties Metric English Comments
Density 1.01 g/cc
0.0365 lb/in³
ASTM D792
Moisture Vapor Transmission 0.600 cc-mm/m²-24hr-atm
1.52 cc-mil/100 in²-24hr-atm
@ 23°C; ASTM F1249
Oxygen Transmission 173 cc-mm/m²-24hr-atm
439 cc-mil/100 in²-24hr-atm
ASTM D3985
Melt Flow 7.5 g/10 min

@Load 5.00 kg,
Temperature 200 °C
7.5 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 26.0 MPa
3770 psi
2 in per min; ASTM D882
Film Tensile Strength at Yield, TD 16.0 MPa
2320 psi
2 in per min; ASTM D882
Film Elongation at Break, MD 65 %
65 %
ASTM D882
Film Elongation at Break, TD 175 %
175 %
ASTM D882
Secant Modulus, MD 1.275 GPa
184.9 ksi
at 1%; ASTM D882
Secant Modulus, TD 0.883 GPa
128 ksi
at 1%; ASTM D882
Elmendorf Tear Strength, MD 0.0217 g/micron
0.550 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 0.0272 g/micron
0.690 g/mil
ASTM D1922
Dart Drop Test 345 g
0.761 lb
26 in; ASTM D1709
Thermal Properties Metric English Comments
Flammability, UL94 HB
HB
Optical Properties Metric English Comments
Haze 2.0 %
2.0 %
ASTM D1003
Gloss 129 %
129 %
45°; ASTM D2457
Transmission, Visible 99 %
99 %
ASTM D1003
Processing Properties Metric English Comments
Melt Temperature 166 - 193 °C
331 - 379 °F
Blown Film