Chevron Phillips MarFlex® 9656 HDPE Blown Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer Chevron Phillips Chemical Company LP
Trade Name MarFlex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chevron Phillips MarFlex® 9656 HDPE Blown Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Resin Type: high density, linear polyethylene.Characteristics: copolymerization enhances film toughness, good drawdown, density level gives good machinability, blend well with LLDPEApplications: notion and millinery bags, multi-wall liners, coextrusionsRecommended processing conditions: Die Gap 0.030-0.050 in. Melt Temperature 400°F.Data provided by Chevron Phillips Chemical Company, LP.
Physical Properties Metric English Comments
Density 0.956 g/cc
0.0345 lb/in³
ASTM D1505
Moisture Vapor Transmission 0.150 cc-mm/m²-24hr-atm
0.381 cc-mil/100 in²-24hr-atm
ASTM F1249
Thickness 31.8 microns
1.25 mil
Melt Flow 0.75 g/10 min
0.75 g/10 min
ASTM D1238E
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 580 %
580 %
ASTM D882
Film Elongation at Break, TD 500 %
500 %
ASTM D882
Elmendorf Tear Strength, MD 0.512 g/micron
13.0 g/mil
Notched; ASTM D1922
Elmendorf Tear Strength, TD 23.6 g/micron
600 g/mil
Notched; ASTM D1992
Dart Drop 1.97 g/micron
50.0 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 51.0 MPa
7400 psi
ASTM D882
Film Tensile Strength at Break, TD 17.9 MPa
2600 psi
ASTM D882
1% Secant Modulus, MD 841 MPa
122000 psi
ASTM D882
1% Secant Modulus, TD 1070 MPa
155000 psi
ASTM D882
Processing Properties Metric English Comments
Processing Temperature 204 °C
399 °F
Die Opening 0.0760 - 0.130 cm
0.0299 - 0.0512 in