Chevron Phillips MarFlex® 9659 HDPE Blown Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer Chevron Phillips Chemical Company LP
Trade Name MarFlex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chevron Phillips MarFlex® 9659 HDPE Blown Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Resin Type: Linear Polyethylene HomopolymerCharacteristics: Unique Molecular Architecture Gives Outstanding Moisture Barrier Properties, Excellent Film Strength and Toughness for a Homopolymer, Gives Paper-like Film Texture, Embosses Extremely Well, Draws to Very Thin Gauges, Excellent Heat Seal StrengthApplications: Food Packaging, Coextrusions, Tissue Paper Replacement, Deli Wrap, Moisture Barrier FilmsFilm properties below based on film thickness of 25.4 µm.Data provided by Chevron Chemical.
Physical Properties Metric English Comments
Density 0.962 g/cc
0.0348 lb/in³
ASTM D1505
Moisture Vapor Transmission 0.100 cc-mm/m²-24hr-atm
0.254 cc-mil/100 in²-24hr-atm
ASTM F1249
Melt Flow 1.0 g/10 min
1.0 g/10 min
Condition E; ASTM D 1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 490 %
490 %
ASTM D882
Film Elongation at Break, TD 550 %
550 %
ASTM D882
Secant Modulus, MD 1.10 GPa
160 ksi
ASTM D882
Secant Modulus, TD 1.20 GPa
174 ksi
ASTM D882
Elmendorf Tear Strength, MD 0.748 g/micron
19.0 g/mil
Notched; ASTM D1922
Elmendorf Tear Strength, TD 8.27 g/micron
210 g/mil
ASTM D1922
Dart Drop 1.40 g/micron
35.6 g/mil
1.5 in. dart/26 in. drop height; ASTM D 1709
Film Tensile Strength at Break, MD 42.0 MPa
6090 psi
ASTM D882
Film Tensile Strength at Break, TD 26.0 MPa
3770 psi
ASTM D882
Processing Properties Metric English Comments
Melt Temperature 210 °C
410 °F