Chevron Phillips MarFlex® HHM TR-130 MDPE Film Resin

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , MDPE , Medium Density Polyethylene (MDPE), Film Grade
Manufacturer	Chevron Phillips Chemical Company LP
Trade Name	MarFlex®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chevron Phillips MarFlex® HHM TR-130 MDPE Film Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Medium density resin provides overall balance of tensile, impact, and tear properties in film. It is suited for merchandise, produce, and trash bags. Processing performance is excellent on high stalk lines. HHM TR-130 meets FDA regulations for food packaging.Data provided by Chevron Phillips Chemical Company, LP.

Physical Properties	Metric	English	Comments
Density	0.937 g/cc	0.0339 lb/in³	ASTM D1505
Thickness	25.4 microns	1.00 mil
Melt Flow	0.30 g/10 min @Load 2.16 kg, Temperature 190 °C	0.30 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
High Load Melt Index	20 g/10 min @Load 21.6 kg, Temperature 190 °C	20 g/10 min @Load 47.6 lb, Temperature 374 °F	HLMI; ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	21.4 MPa	3100 psi	ASTM D882
Film Tensile Strength at Yield, TD	21.4 MPa	3100 psi	ASTM D882
Film Elongation at Break, MD	500 %	500 %	ASTM D882
Film Elongation at Break, TD	600 %	600 %	ASTM D882
Elmendorf Tear Strength, MD	1.97 g/micron	50.0 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	19.7 g/micron	500 g/mil	ASTM D1922
Dart Drop	5.12 g/micron	130 g/mil	26 in (66 cm); ASTM D1709
Film Tensile Strength at Break, MD	42.1 MPa	6100 psi	ASTM D882
Film Tensile Strength at Break, TD	42.1 MPa	6100 psi	ASTM D882

Processing Properties	Metric	English	Comments
Processing Temperature	216 °C	421 °F
Die Opening	0.0890 cm	0.0350 in