Chevron Phillips Marlex® 7104 LLDPE Sheet Extrusion

Category	Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Extrusion Grade
Manufacturer	Chevron Phillips Chemical Company LP
Trade Name	Marlex®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chevron Phillips Marlex® 7104 LLDPE Sheet Extrusion.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Resin Type: Hexene CopolymerCharacteristics: Outstanding ESCRGood melt strengthExcellent flexibilityGood processabilityGood glossHigh COFApplications: Landfill coversFlat and round-die productsCoextruded cap layers on HDPEBlends with HDPEInformation provided by Chevron Phillips.

Physical Properties	Metric	English	Comments
Density	0.918 g/cc	0.0332 lb/in³	ASTM D1505
ESCR 100% Igepal®	>= 2000 hour	>= 2000 hour	ASTM D1693
ESCR 10% Igepal®	>= 2000 hour	>= 2000 hour	ASTM D1693
Oxidative Induction Time (OIT)	>= 100 min	>= 100 min	ASTM D3895
Melt Index of Compound	0.35 g/10 min	0.35 g/10 min	Condition 190/2.16; ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	51	51	ASTM D2240
Tensile Strength, Yield	11.0 MPa	1600 psi	2 in/min, Type IV bar; ASTM D638
Elongation at Break	700 %	700 %	2 in/min, Type IV bar; ASTM D638
Flexural Modulus	0.410 GPa	59.5 ksi	ASTM D790
Tensile Impact Strength	NB	NB	Type S bar; ASTM D1822

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	51.0 °C	124 °F	ASTM D648
Vicat Softening Point	100 °C	212 °F	Loading 1, Rate A; ASTM D1525
Brittleness Temperature	<= -75.0 °C	<= -103 °F	Type A, type 1 specimen; ASTM D746

Descriptive Properties	Value	Comments
SP-NCTL	Min 1000	Single-point notched constant tensile load

Users viewing this material also viewed the following: