Chevron Phillips Ryton® A-200 PPS Polyphenylene Sulfide  (discontinued **)

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chevron Phillips Ryton® A-200 PPS Polyphenylene Sulfide  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ryton® PPS is used in many electronic and automotive applications because of its high strength, favorable electrical properties, and high temperature stability.Data provided by the manufacturer.Solvay Specialty Polymers has acquired the Ryton product line. This product was discontinued prior to the acquisition and is listed under the Chevron Phillips name for historical purposes.
Physical Properties Metric English Comments
Density 1.60 g/cc
0.0578 lb/in³
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
Tensile Strength, Ultimate 120 MPa
17400 psi
ASTM D638
Tensile Strength, Yield 120 MPa
17400 psi
ASTM D638
Elongation at Break 1.0 %
1.0 %
ASTM D638
Modulus of Elasticity 13.0 GPa
1890 ksi
ASTM D638
Flexural Yield Strength 170 MPa
24700 psi
ASTM D790
Flexural Modulus 12.0 GPa
1740 ksi
ASTM D790
Compressive Yield Strength 170 MPa
24700 psi
ASTM D695
Poissons Ratio 0.396
0.396
Shear Modulus 4.66 GPa
676 ksi
Calculated
Shear Strength 82.7 MPa
12000 psi
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched 2.40 J/cm
4.50 ft-lb/in
ASTM D256
Taber Abrasion, mg/1000 Cycles 23
23
CS-17 wheel; 1 kg
Thermal Properties Metric English Comments
CTE, linear 18.0 µm/m-°C

@Temperature -100 °C
10.0 µin/in-°F

@Temperature -148 °F
20.0 µm/m-°C

@Temperature 250 °C
11.1 µin/in-°F

@Temperature 482 °F
35.0 µm/m-°C

@Temperature 20.0 °C
19.4 µin/in-°F

@Temperature 68.0 °F
In machine direction.
CTE, linear, Transverse to Flow 25.0 µm/m-°C

@Temperature -100 °C
13.9 µin/in-°F

@Temperature -148 °F
35.0 µm/m-°C

@Temperature 20.0 °C
19.4 µin/in-°F

@Temperature 68.0 °F
60.0 µm/m-°C

@Temperature 250 °C
33.3 µin/in-°F

@Temperature 482 °F
Thermal Conductivity 0.320 W/m-K

@Temperature 90.0 °C
2.22 BTU-in/hr-ft²-°F

@Temperature 194 °F
Melting Point 285 °C
545 °F
Deflection Temperature at 1.8 MPa (264 psi) >= 260 °C
>= 500 °F
Estimated from similar grades. ASTM D648
Glass Transition Temp, Tg 88.0 °C
190 °F
Flammability, UL94 5VA
5VA
V-0/5VA UL-94 Rating (value for most Ryton® grades)
Oxygen Index 50 %
50 %
Estimated from similar grades.; ASTM D2863
Electrical Properties Metric English Comments
Electrical Resistivity 1.40e+15 ohm-cm
1.40e+15 ohm-cm
ASTM D257
Insulation Resistance 1.00e+11 ohm
1.00e+11 ohm
Accelerated; 194°F; 95% RH; 2 days; ASTM D257
Dielectric Strength 19.1 kV/mm
485 kV/in
ASTM D149
Processing Properties Metric English Comments
Melt Temperature 304 - 343 °C
579 - 649 °F