Chi Mei Polyrex® PH-88S Polystyrene - Extrusion
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Extrusion Grade |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polyrex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polyrex® PH-88S Polystyrene - Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Extrusion
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Melt Flow | 3.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
3.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 76.0 MPa | 11000 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 24.0 MPa | 3480 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 66 % | 66 % | 50 mm/min; ISO 527 |
| Flexural Strength | 34.0 MPa | 4930 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.40 GPa | 203 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/1C |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179 |
| Impact | 14.0 | 14.0 | Impact Flexural Test Notched (KJ/m²) |
| 100 | 100 | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | unannealed; ISO 75 |
| 94.0 °C | 201 °F | annealed; ISO 75 | |
| Vicat Softening Point | 89.0 °C @Load 5.00 kg |
192 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 93.0 °C @Load 5.00 kg |
199 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 100 °C @Load 1.00 kg |
212 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 104 °C @Load 1.00 kg |
219 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL 94 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics GELOY HRA222 ASA (Asia Pacific)
- Victrex® Vicote® F817 Polyetheretherketone (PEEK) Liquid Dispersion, Enhanced Adhesion Grade
- Eastman 5290 LDPE High Clarity, Ultra-High Impact Film Resin, 12% EVA Copolymer (discontinued **)
- PolyOne Geon™ Vinyl Flexible R158AE Polyvinyl Chloride, Flexible (PVC, Flexible)
- LyondellBasell Petrothene® NA217000 Low Density Polyethylene
- SGL Carbon Group PANOX® SA C063 SSC High performance oxidized textile fiber, Crimped staple fiber, For felts and non-wovens
- Eifeler Coatings Technology TiN PVD Coating
- Chem Polymer Durlex 709 IH PBT, Impact Modified
- KKPC KOSYN KSL 5153 Styrene-Butadiene Latex
Copyright © lookpolymers.com All Rights Reserved