Clariant 6618G15 HSL UV Black Nylon 66, 15% Glass Fiber, Impact Modified, UV and Heat Stabilized, Lubricated
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled , Nylon 66, Glass Reinforced, Impact Grade |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant 6618G15 HSL UV Black Nylon 66, 15% Glass Fiber, Impact Modified, UV and Heat Stabilized, Lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Filler Content | 15 % | 15 % | ASTM D2584 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 68.9 MPa | 10000 psi | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Yield Strength | 103 MPa | 15000 psi | ASTM D790 |
| Flexural Modulus | 2.62 GPa | 380 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm @Temperature 22.8 °C |
1.30 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 470 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 288 °C | 500 - 550 °F | |
| Middle Barrel Temperature | 260 - 288 °C | 500 - 550 °F | |
| Front Barrel Temperature | 266 - 293 °C | 510 - 560 °F | |
| Nozzle Temperature | 266 - 293 °C | 510 - 560 °F | |
| Melt Temperature | 266 - 288 °C | 510 - 550 °F | |
| Mold Temperature | 54.4 - 82.2 °C | 130 - 180 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Amodel® AP-9240 NL Polyphthalamide (PPA) Resin, 40% Mineral Filled, Dry as Molded (
- Solvay Specialty Polymers Cogegum® GFR/360 Polyolefin, Unspecified (Unverified Data**)
- SABIC Innovative Plastics Cycoloy® C1200HF PC+ABS (Europe-Africa-Middle East)
- LyondellBasell Plexar® PX2413 Extrudable Tie-Layer Resin, Anhydride Modified LLDPE
- Universal Wire Works 17-7 (AMS 5824) Filler Metal
- EMS-Griltech Grilon® BA 115 White Nylon 6/CoPA Bi-Component Fiber
- Arkema Group KYNAR® 740 Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion
- Axiall 19940 Wire & Cable Flexible PVC
- Dow Corning 2-9138 RESIN
Copyright © lookpolymers.com All Rights Reserved