Constellium Certal® Thick Aluminum Plate

Category Metal , Nonferrous Metal , Aluminum Alloy , 7000 Series Aluminum Alloy
Manufacturer Constellium
Trade Name Certal®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Constellium Certal® Thick Aluminum Plate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Certal® thick plates have been optimized to provide excellent machinability, shape stability and high strength. Certal® is therefore ideal for industrial tools. Applications include injection and blow-moulds for plastic bottles, containers, shoes as well as heating plates, guides, tooling supports, jigs and fixtures.Information provided by manufacturer
Physical Properties Metric English Comments
Density 2.76 g/cc
0.0997 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 165

@Thickness 25.0 - 100 mm
 165

@Thickness 0.984 - 3.94 in
165

@Thickness 100 - 140 mm
 165

@Thickness 3.94 - 5.51 in
170

@Thickness 7.90 - 25.0 mm
 170

@Thickness 0.311 - 0.984 in
Tensile Strength >= 490 MPa

@Thickness 100 - 140 mm
 >= 71100 psi

@Thickness 3.94 - 5.51 in
 Temper T651
>= 500 MPa

@Thickness 50.0 - 100 mm
 >= 72500 psi

@Thickness 1.97 - 3.94 in
 Temper T651
>= 530 MPa

@Thickness 25.0 - 50.0 mm
 >= 76900 psi

@Thickness 0.984 - 1.97 in
 Temper T651
>= 540 MPa

@Thickness 7.90 - 12.5 mm
 >= 78300 psi

@Thickness 0.311 - 0.492 in
 Temper T651
>= 540 MPa

@Thickness 12.5 - 25.0 mm
 >= 78300 psi

@Thickness 0.492 - 0.984 in
 Temper T651
545 MPa

@Thickness 100 - 140 mm
 79000 psi

@Thickness 3.94 - 5.51 in
 Typical Strength
550 MPa

@Thickness 25.0 - 100 mm
 79800 psi

@Thickness 0.984 - 3.94 in
 Typical Strength
555 MPa

@Thickness 7.90 - 25.0 mm
 80500 psi

@Thickness 0.311 - 0.984 in
 Typical Strength
Tensile Strength, Yield >= 400 MPa

@Strain 0.200 %,
Thickness 100 - 140 mm
 >= 58000 psi

@Strain 0.200 %,
Thickness 3.94 - 5.51 in
 Temper T651
>= 420 MPa

@Strain 0.200 %,
Thickness 50.0 - 100 mm
 >= 60900 psi

@Strain 0.200 %,
Thickness 1.97 - 3.94 in
 Temper T651
>= 460 MPa

@Strain 0.200 %,
Thickness 7.90 - 12.5 mm
 >= 66700 psi

@Strain 0.200 %,
Thickness 0.311 - 0.492 in
 Temper T651
>= 460 MPa

@Strain 0.200 %,
Thickness 12.5 - 25.0 mm
 >= 66700 psi

@Strain 0.200 %,
Thickness 0.492 - 0.984 in
 Temper T651
>= 460 MPa

@Strain 0.200 %,
Thickness 25.0 - 50.0 mm
 >= 66700 psi

@Strain 0.200 %,
Thickness 0.984 - 1.97 in
 Temper T651
490 MPa

@Strain 0.200 %,
Thickness 100 - 140 mm
 71100 psi

@Strain 0.200 %,
Thickness 3.94 - 5.51 in
 Typical Strength
495 MPa

@Strain 0.200 %,
Thickness 7.90 - 25.0 mm
 71800 psi

@Strain 0.200 %,
Thickness 0.311 - 0.984 in
 Typical Strength
495 MPa

@Strain 0.200 %,
Thickness 25.0 - 100 mm
 71800 psi

@Strain 0.200 %,
Thickness 0.984 - 3.94 in
 Typical Strength
Elongation at Break >= 6.0 %

@Thickness 50.0 - 100 mm
 >= 6.0 %

@Thickness 1.97 - 3.94 in
 Temper T651
>= 6.0 %

@Thickness 100 - 140 mm
 >= 6.0 %

@Thickness 3.94 - 5.51 in
 Temper T651
>= 7.0 %

@Thickness 25.0 - 50.0 mm
 >= 7.0 %

@Thickness 0.984 - 1.97 in
 Temper T651
7.0 %

@Thickness 100 - 140 mm
 7.0 %

@Thickness 3.94 - 5.51 in
 Typical Elongation
8.0 %

@Thickness 25.0 - 100 mm
 8.0 %

@Thickness 0.984 - 3.94 in
 Typical Elongation
>= 8.0 %

@Thickness 7.90 - 12.5 mm
 >= 8.0 %

@Thickness 0.311 - 0.492 in
 Temper T651
>= 8.0 %

@Thickness 12.5 - 25.0 mm
 >= 8.0 %

@Thickness 0.492 - 0.984 in
 Temper T651
9.0 %

@Thickness 7.90 - 25.0 mm
 9.0 %

@Thickness 0.311 - 0.984 in
 Typical Elongation
Modulus of Elasticity 72.0 GPa
10400 ksi
Thermal Properties Metric English Comments
CTE, linear 23.6 µm/m-°C

@Temperature 20.0 - 100 °C
 13.1 µin/in-°F

@Temperature 68.0 - 212 °F
Thermal Conductivity 120 - 150 W/m-K
833 - 1040 BTU-in/hr-ft²-°F
Temper T651
Component Elements Properties Metric English Comments
Aluminum, Al 88.2 - 92.4 %
88.2 - 92.4 %
as balance
Chromium, Cr 0.10 - 0.30 %
0.10 - 0.30 %
Copper, Cu 0.50 - 1.0 %
0.50 - 1.0 %
Iron, Fe <= 0.50 %
<= 0.50 %
Magnesium, Mg 2.6 - 3.7 %
2.6 - 3.7 %
Manganese, Mn 0.10 - 0.40 %
0.10 - 0.40 %
Silicon, Si <= 0.50 %
<= 0.50 %
Zinc, Zn 4.3 - 5.2 %
4.3 - 5.2 %
Zr+Ti <= 0.20 %
<= 0.20 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000450 - 0.00000550 ohm-cm
0.00000450 - 0.00000550 ohm-cm
Temper T651