Cookson Group Plaskon® 3200LS Mineral Filled Novolac Epoxy Molding Compound (discontinued **)

Category	Polymer , Thermoset , Epoxy , Epoxy, Molded, Mineral Filled , Filled/Reinforced Thermoset
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Cookson Group Plaskon® 3200LS Mineral Filled Novolac Epoxy Molding Compound (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Test specimens were transfer molded and post cured 4 hours at 175°C.Exhibits exceptional reliability under very stringent testing. This material is designed to minimize stress on the encapsulated device due to its low stress characteristics.

Physical Properties	Metric	English	Comments
Density	1.86 g/cc	0.0672 lb/in³
Spiral Flow	64.0 - 88.0 cm	25.2 - 34.6 in	177°C/1000 psi

Mechanical Properties	Metric	English
Hardness, Shore D	75	75
Tensile Strength, Ultimate	90.0 MPa	13100 psi
Flexural Strength	121 MPa	17500 psi

Thermal Properties	Metric	English
CTE, linear	22.0 µm/m-°C @Temperature 20.0 °C	12.2 µin/in-°F @Temperature 68.0 °F
CTE, linear, Transverse to Flow	70.0 µm/m-°C @Temperature 20.0 °C	38.9 µin/in-°F @Temperature 68.0 °F
Thermal Conductivity	0.700 W/m-K	4.86 BTU-in/hr-ft²-°F
Glass Transition Temp, Tg	155 °C	311 °F
Flammability, UL94	V-0 @Thickness 3.20 mm	V-0 @Thickness 0.126 in
	V-0 @Thickness 3.20 mm	V-0 @Thickness 0.126 in

Electrical Properties	Metric	English
Dielectric Constant	3.91 @Frequency 1000 Hz	3.91 @Frequency 1000 Hz
Dielectric Strength	18.0 kV/mm	457 kV/in
Dissipation Factor	0.0010 @Frequency 1000 Hz	0.0010 @Frequency 1000 Hz
Arc Resistance	190 sec	190 sec

Processing Properties	Metric	English	Comments
Processing Temperature	171 - 193 °C	340 - 379 °F	Molding temperature