Material Notes:
Test specimens were transfer molded and post cured 4 hours at 175°C.A fast curing, reduced-stress epoxy molding compound for the encapsulation of semiconductor devices including DIPs, PLCCs, SOICs and medium lead count QFPs. Fast cycle times; Excellent moldability (ease of filling, good release, minimal flash and bleed and good hot hardness); Superior cosmetics; Improved markability
Physical Properties Metric English Comments
Density 1.80 g/cc
0.0650 lb/in³
Viscosity 26000 - 34000 cP

@Temperature 175 °C
26000 - 34000 cP

@Temperature 347 °F
Automatic orifice Viscosity
Spiral Flow 48.0 - 62.0 cm
18.9 - 24.4 in
177°C/1000 psi
Mechanical Properties Metric English Comments
Hardness, Shore D 70
70
Flexural Strength 124 MPa
18000 psi
Flexural Modulus 15.0 GPa
2180 ksi
Thermal Properties Metric English Comments
CTE, linear 22.0 µm/m-°C

@Temperature 20.0 °C
12.2 µin/in-°F

@Temperature 68.0 °F
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature 20.0 °C
33.3 µin/in-°F

@Temperature 68.0 °F
Thermal Conductivity 0.700 W/m-K
4.86 BTU-in/hr-ft²-°F
Glass Transition Temp, Tg 145 °C
293 °F
Flammability, UL94 V-0

@Thickness 3.20 mm
V-0

@Thickness 0.126 in
V-0

@Thickness 3.20 mm
V-0

@Thickness 0.126 in
Electrical Properties Metric English Comments
Dielectric Constant 3.8

@Frequency 1000 Hz
3.8

@Frequency 1000 Hz
Dielectric Strength 16.0 kV/mm
406 kV/in
Dissipation Factor 0.0020

@Frequency 1000 Hz
0.0020

@Frequency 1000 Hz
Arc Resistance 180 sec
180 sec
Processing Properties Metric English Comments
Processing Temperature 170 - 185 °C
338 - 365 °F
Molding temperature