Cossa Polimeri ESTABLEND 4501 V0/D Flame Retardant PC - ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Cossa Polimeri S.r.L.
Trade Name ESTABLEND
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Cossa Polimeri ESTABLEND 4501 V0/D Flame Retardant PC - ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PC - ABS BlendFlame retardant class V0, PBDE and antimony free, with halogens, high impact resistance, very high thermal resistance, high gloss, good processabilityInformation provided by Cossa Polimeri S.r.l.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ASTM D 792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D 955
Melt Flow 28 g/10 min

@Load 5.00 kg,
Temperature 260 °C
28 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
ASTM D 638
Tensile Strength, Yield 63.0 MPa
9140 psi
ASTM D 638
Elongation at Break >= 50 %
>= 50 %
ASTM D 638
Flexural Modulus 2.50 GPa
363 ksi
ASTM D 790
Izod Impact, Notched 5.00 J/cm

@Temperature 0.000 °C
9.37 ft-lb/in

@Temperature 32.0 °F
ASTM D 638
5.50 J/cm

@Temperature 23.0 °C
10.3 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Thermal Properties Metric English Comments
Hot Ball Pressure Test 125 °C
257 °F
I.E.C. 335-1
Vicat Softening Point 144 °C

@Load 5.00 kg
291 °F

@Load 11.0 lb
50°C/hr; ASTM D 1525
148 °C

@Load 0.999 kg
298 °F

@Load 2.20 lb
50°C/hr; ASTM D 1525
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
V-0

@Thickness 3.20 mm
V-0

@Thickness 0.126 in
Glow Wire Test 960 °C
1760 °F
I.E.C. 695-2-1