Cossa Polimeri ESTADIENE 4009 Acrylonitrile Butadiene Styrene

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
Manufacturer Cossa Polimeri S.r.L.
Trade Name ESTADIENE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Cossa Polimeri ESTADIENE 4009 Acrylonitrile Butadiene Styrene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ABS with high impact resistanceHigh impact resistance at low temperature, high gloss, good processabilityInformation provided by Cossa Polimeri S.r.l.
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ASTM D 792
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ASTM D 955
Melt Flow 9.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
9.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 24.0 MPa
3480 psi
ASTM D 638
Tensile Strength, Yield 31.0 MPa
4500 psi
ASTM D 638
Elongation at Break 4.2 %
4.2 %
ASTM D 638
Flexural Modulus 1.80 GPa
261 ksi
ASTM D 790
Izod Impact, Notched 3.00 J/cm

@Temperature -20.0 °C
5.62 ft-lb/in

@Temperature -4.00 °F
ASTM D 638
3.80 J/cm

@Temperature 0.000 °C
7.12 ft-lb/in

@Temperature 32.0 °F
ASTM D 638
4.30 J/cm

@Temperature 23.0 °C
8.06 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Thermal Properties Metric English Comments
Vicat Softening Point 96.0 °C

@Load 5.00 kg
205 °F

@Load 11.0 lb
50°C/hr; ASTM D 1525
106 °C

@Load 0.999 kg
223 °F

@Load 2.20 lb
50°C/hr; ASTM D 1525
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Glow Wire Test 650 °C

@Thickness 2.00 mm
1200 °F

@Thickness 0.0787 in
I.E.C. 695-2-1