Cossa Polimeri ESTAPROP 1006 V2 K Flame Retardant Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene, Flame Retardant
Manufacturer Cossa Polimeri S.r.L.
Trade Name ESTAPROP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Cossa Polimeri ESTAPROP 1006 V2 K Flame Retardant Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PP copolymerFlame retardant class V2, PBDE and antimony trioxide free, no blooming, low smoke emission, good physical and mechanical characteristicsInformation provided by Cossa Polimeri S.r.l.
Physical Properties Metric English Comments
Density 0.930 g/cc
0.0336 lb/in³
ASTM D 792
Linear Mold Shrinkage 0.015 - 0.018 cm/cm
0.015 - 0.018 in/in
ASTM D 955
Melt Flow 20 g/10 min

@Load 2.16 kg,
Temperature 230 °C
20 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 28.0 MPa
4060 psi
ASTM D 638
Elongation at Break 100 %
100 %
ASTM D 638
Flexural Modulus 1.40 GPa
203 ksi
ASTM D 790
Izod Impact, Notched 0.400 J/cm

@Temperature -20.0 °C
0.749 ft-lb/in

@Temperature -4.00 °F
ASTM D 638
0.500 J/cm

@Temperature 0.000 °C
0.937 ft-lb/in

@Temperature 32.0 °F
ASTM D 638
0.600 J/cm

@Temperature 23.0 °C
1.12 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
120°C/hr; ASTM D 648
Vicat Softening Point 150 °C

@Load 0.999 kg
302 °F

@Load 2.20 lb
50°C/hr; ASTM D 1525
Flammability, UL94 V-2

@Thickness 1.60 mm
V-2

@Thickness 0.0630 in
V-2

@Thickness 3.20 mm
V-2

@Thickness 0.126 in
Glow Wire Test 960 °C

@Thickness 2.00 mm
1760 °F

@Thickness 0.0787 in
I.E.C. 695-2-1