Covestro Bayblend® FR 90 N Polycarbonate/ABS Blend

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Covestro
Trade Name Bayblend®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Bayblend® FR 90 N Polycarbonate/ABS Blend.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Flame retardant grade with antimony, chlorine and bromine free, flame retardant package, optimized processability.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
Water Absorption 0.70 %
0.70 %
Saturation in water
Moisture Absorption at Equilibrium 0.20 %
0.20 %
Equilibrium at 50% RH
Water Absorption at Saturation 0.70 %
0.70 %
Melt Flow 20 g/10 min

@Load 5.00 kg,
Temperature 240 °C
20 g/10 min

@Load 11.0 lb,
Temperature 464 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 60.0 MPa
8700 psi
Elongation at Break >= 50 %
>= 50 %
Nominal
Elongation at Yield 4.0 %
4.0 %
Tensile Modulus 2.80 GPa
406 ksi
Tensile Creep Modulus, 1 hour 2500 MPa
363000 psi
Tensile Creep Modulus, 1000 hours 1900 MPa
276000 psi
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 69.0 µm/m-°C

@Temperature 20.0 °C
38.3 µin/in-°F

@Temperature 68.0 °F
CTE, linear, Transverse to Flow 76.0 µm/m-°C

@Temperature 20.0 °C
42.2 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C
194 °F
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C
176 °F
Vicat Softening Point 92.0 °C
198 °F
UL RTI, Electrical 85.0 °C

@Thickness 1.00 mm
185 °F

@Thickness 0.0394 in
UL RTI, Mechanical with Impact 75.0 °C

@Thickness 1.50 mm
167 °F

@Thickness 0.0591 in
UL RTI, Mechanical without Impact 80.0 °C

@Thickness 1.50 mm
176 °F

@Thickness 0.0591 in
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
Oxygen Index 30 %
30 %
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
Dielectric Constant 2.9

@Frequency 1e+6 Hz
2.9

@Frequency 1e+6 Hz
3.0

@Frequency 100 Hz
3.0

@Frequency 100 Hz
Dielectric Strength 30.0 kV/mm
762 kV/in
Dissipation Factor 0.0050

@Frequency 100 Hz
0.0050

@Frequency 100 Hz
0.0070

@Frequency 1e+6 Hz
0.0070

@Frequency 1e+6 Hz
Arc Resistance 60 - 120 sec

@Thickness 3.00 mm
60 - 120 sec

@Thickness 0.118 in
UL Rating PLC 6 (60-120 sec)
Comparative Tracking Index 300 V
300 V
Hot Wire Ignition, HWI 60 - 120 sec

@Thickness 3.00 mm
60 - 120 sec

@Thickness 0.118 in
UL Rating PLC 1 (60-120 sec)
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 1.50 mm
>= 120 arcs

@Thickness 0.0591 in
UL Rating PLC 0 (>120 arcs)
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min

@Thickness 3.00 mm
>= 5.91 in/min

@Thickness 0.118 in
UL Rating PLC 4 (>150 mm/min.)