Covestro Bayblend® SF 1443 Polycarbonate + ABS Blend Structural Foam  (discontinued **)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Bayblend® SF 1443 Polycarbonate + ABS Blend Structural Foam  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Foam thickness 0.250 in. Properties values at foam density of 0.90 g/cc.Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This product was discontinued prior to the separation.
Physical Properties Metric English Comments
Density 0.900 g/cc
0.0325 lb/in³
Foam; ASTM D792
1.18 g/cc
0.0426 lb/in³
Solid; ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 42.0 MPa
6090 psi
ASTM D638
Elongation at Break 3.4 %
3.4 %
ASTM D638
Flexural Yield Strength 80.0 MPa
11600 psi
at 5% strain; ASTM D790
Flexural Modulus 2.62 GPa
380 ksi
ASTM D790
Impact Test 30.0 J

@Thickness 3.20 mm
22.1 ft-lb

@Thickness 0.126 in
Instrumented Impact, Total Energy; 3.2 mm thick, 2.5 mph, 3 in. clamp, 0.5 in. dart; ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 94.0 °C

@Thickness 6.35 mm
201 °F

@Thickness 0.250 in
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 77.0 °C

@Thickness 6.35 mm
171 °F

@Thickness 0.250 in
ASTM D648
UL RTI, Electrical 60.0 °C

@Thickness 3.00 mm
140 °F

@Thickness 0.118 in
UL RTI, Mechanical with Impact 60.0 °C

@Thickness 3.00 mm
140 °F

@Thickness 0.118 in
UL RTI, Mechanical without Impact 60.0 °C

@Thickness 3.00 mm
140 °F

@Thickness 0.118 in
Flammability, UL94 V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in