Covestro Makrolon® 1881 Polycarbonate

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Impact Modified , Polycarbonate, Molded , Polycarbonate, UV Stabilized
Manufacturer Covestro
Trade Name Makrolon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Makrolon® 1881 Polycarbonate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Impact modified• Improved ultrasonic weldability• UV stabilized• Low viscosity, easy release • Injection moldingAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Physical Properties Metric English Comments
Bulk Density 0.640 g/cc
0.0231 lb/in³
pellets; ISO 60
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183-1
Moisture Absorption at Equilibrium 0.12 %
0.12 %
ISO 62, 50% RH
Water Absorption at Saturation 0.30 %
0.30 %
ISO 62
Linear Mold Shrinkage, Flow 0.0065 cm/cm

@Thickness 2.00 mm
0.0065 in/in

@Thickness 0.0787 in
60x60x2 mm; 500 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0070 cm/cm

@Thickness 2.00 mm
0.0070 in/in

@Thickness 0.0787 in
60x60x2 mm; 500 bar; ISO 294-4
Melt Flow 20 g/10 min

@Load 1.20 kg,
Temperature 300 °C
20 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ISO 1133
Mechanical Properties Metric English Comments
Puncture Resistance 4900 N

@Temperature 23.0 °C
1100 lb (f)

@Temperature 73.4 °F
ISO 6603-2
5800 N

@Temperature -30.0 °C
1300 lb (f)

@Temperature -22.0 °F
ISO 6603-2
Ball Indentation Hardness 113 MPa
16400 psi
ISO 2039-1
Tensile Strength at Break 60.0 MPa
8700 psi
50 mm/min; ISO 527-1,-2
Tensile Strength, Yield 60.0 MPa
8700 psi
50 mm/min; ISO 527-1,-2
Elongation at Break >= 50 %
>= 50 %
Nominal, 50 mm/min; ISO 527-1,-2
110 %
110 %
50 mm/min; b.o. ISO 527-1,-2
Elongation at Yield 5.8 %
5.8 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 2.30 GPa
334 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 93.0 MPa
13500 psi
2 mm/min; ISO 178
Flexural Yield Strength 70.0 MPa

@Strain 3.50 %
10200 psi

@Strain 3.50 %
2 mm/min; ISO 178
Flexural Modulus 2.30 GPa
334 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 14.0 kJ/m²

@Thickness 3.20 mm,
Temperature -30.0 °C
6.66 ft-lb/in²

@Thickness 0.126 in,
Temperature -22.0 °F
complete break; b.o. ISO 180-A
70.0 kJ/m²

@Thickness 3.20 mm,
Temperature 23.0 °C
33.3 ft-lb/in²

@Thickness 0.126 in,
Temperature 73.4 °F
partial break; b.o. ISO 180-A
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179-1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179-1eU
NB

@Temperature -60.0 °C
NB

@Temperature -76.0 °F
ISO 179-1eU
Charpy Impact, Notched 1.40 J/cm²

@Thickness 3.00 mm,
Temperature -30.0 °C
6.66 ft-lb/in²

@Thickness 0.118 in,
Temperature -22.0 °F
complete break; ISO 7391/b.o. ISO 179-1eA
6.00 J/cm²

@Thickness 3.00 mm,
Temperature 23.0 °C
28.6 ft-lb/in²

@Thickness 0.118 in,
Temperature 73.4 °F
partial break; ISO 7391/b.o. ISO 179-1eA
Puncture Energy 50.0 J

@Temperature 23.0 °C
36.9 ft-lb

@Temperature 73.4 °F
ISO 6603-2
55.0 J

@Temperature -30.0 °C
40.6 ft-lb

@Temperature -22.0 °F
ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 65.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
36.1 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1,-2
CTE, linear, Transverse to Flow 65.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
36.1 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1,-2
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
cross-flow; ISO 8302
Hot Ball Pressure Test 134 °C
273 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 136 °C
277 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 123 °C
253 °F
ISO 75-1,-2
Vicat Softening Point 144 °C

@Load 5.10 kg
291 °F

@Load 11.2 lb
50°C/h; ISO 306
145 °C

@Load 5.10 kg
293 °F

@Load 11.2 lb
120°C/h; ISO 306
Flash Point 460 °C
860 °F
ASTM D 1929
540 °C
1000 °F
self ignition; ASTM D 1929
Oxygen Index 30 %
30 %
Method A; IEC 4589-2
Glow Wire Test 825 °C

@Thickness 0.750 mm
1520 °F

@Thickness 0.0295 in
GWIT; IEC 60695-2-13
825 °C

@Thickness 1.50 mm
1520 °F

@Thickness 0.0591 in
GWIT; IEC 60695-2-13
850 °C

@Thickness 3.00 mm
1560 °F

@Thickness 0.118 in
GWIT; IEC 60695-2-13
850 °C

@Thickness 0.750 mm
1560 °F

@Thickness 0.0295 in
GWFI; IEC 60695-2-12
850 °C

@Thickness 1.50 mm
1560 °F

@Thickness 0.0591 in
GWFI; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
GWFI; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
IEC 60093
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
IEC 60093
Dielectric Constant 3.0

@Frequency 1.00e+6 Hz
3.0

@Frequency 1.00e+6 Hz
IEC 60250
3.1

@Frequency 100 Hz
3.1

@Frequency 100 Hz
IEC 60250
Dielectric Strength 34.0 kV/mm

@Thickness 1.00 mm
864 kV/in

@Thickness 0.0394 in
IEC 60243-1
Dissipation Factor 0.0010

@Frequency 100 Hz
0.0010

@Frequency 100 Hz
IEC 60250
0.0105

@Frequency 1.00e+6 Hz
0.0105

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 125 V
125 V
CTI M; Solution B; IEC 60112
250 V
250 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 280 °C
536 °F
Injection molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection molding; ISO 294
Injection Velocity 200 mm/sec
7.87 in/sec
ISO 294
Descriptive Properties Value Comments
Electrolytic Corrosion A1
IEC 60426