Category | Other Engineering Material , Composite Core Material , Wood and Natural Products , Wood |
Manufacturer | DIAB Inc. |
Trade Name | ProBalsa® |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | DIAB ProBalsa® LD7 Light Weight Balsa Wood.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.0900 g/cc | 0.00325 lb/in³ | ASTM C271 |
Moisture Absorption at Equilibrium | 12 % | 12 % |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 7.00 MPa | 1020 psi | ASTM C297 |
Compressive Strength | 5.40 MPa | 783 psi | ASTM C365 |
Compressive Modulus | 1.85 GPa | 268 ksi | ASTM C365 |
Shear Modulus | 0.0960 GPa | 13.9 ksi | ASTM C273 |
Shear Strength | 1.60 MPa | 232 psi | ASTM C273 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 3.60 µm/m-°C | 2.00 µin/in-°F | Longitudinal; ASTM D696 |
14.4 µm/m-°C | 8.00 µin/in-°F | Radial; ASTM D696 | |
21.6 µm/m-°C | 12.0 µin/in-°F | Tangential; ASTM D696 | |
Thermal Conductivity | 0.0520 W/m-K @Temperature 10.0 °C |
0.361 BTU-in/hr-ft²-°F @Temperature 50.0 °F |
ASTM C377 |
Insulation R Value | 1.4 @Thickness 12.0 mm |
1.4 @Thickness 0.472 in |
Based on +10°K factor |
2.9 @Thickness 25.0 mm |
2.9 @Thickness 0.984 in |
Based on +10°K factor | |
5.7 @Thickness 51.0 mm |
5.7 @Thickness 2.01 in |
Based on +10°K factor |