DSM Akulon® Ultraflow K-FKGS6 /B PA6-GF30 FR(17)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer DSM Engineering Plastics
Trade Name Akulon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DSM Akulon® Ultraflow K-FKGS6 /B PA6-GF30 FR(17).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% Glass Reinforced, Heat Stabilized, Flame Retardant, High Flow
Physical Properties Metric English Comments
Density 1.59 g/cc
0.0574 lb/in³
dry; ISO 1183
Water Absorption 4.5 %
4.5 %
Sim. To ISO 62
Moisture Absorption 1.30 %
1.30 %
Sim. To ISO 62
Linear Mold Shrinkage, Flow 0.0021 cm/cm
0.0021 in/in
Sim. To ISO 294-4
Linear Mold Shrinkage, Transverse 0.0077 cm/cm
0.0077 in/in
Sim. To ISO 294
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 100 MPa
14500 psi
cond; ISO 527-1/-2
150 MPa
21800 psi
dry; ISO 527-1/-2
Elongation at Break 2.5 %
2.5 %
dry; ISO 527-1/-2
5.0 %
5.0 %
cond; ISO 527-1/-2
Tensile Modulus 7.03 GPa
1020 ksi
cond; ISO 527-1/-2
11.5 GPa
1670 ksi
dry; ISO 527-1/-2
Charpy Impact Unnotched 5.98 J/cm²

@Temperature 23.0 °C
28.5 ft-lb/in²

@Temperature 73.4 °F
cond; ISO 179/1eU
5.98 J/cm²

@Temperature -30.0 °C
28.5 ft-lb/in²

@Temperature -22.0 °F
cond; ISO 179/1eU
5.98 J/cm²

@Temperature 23.0 °C
28.5 ft-lb/in²

@Temperature 73.4 °F
dry; ISO 179/1eU
5.98 J/cm²

@Temperature -30.0 °C
28.5 ft-lb/in²

@Temperature -22.0 °F
dry; ISO 179/1eU
Charpy Impact, Notched 1.20 J/cm²

@Temperature -30.0 °C
5.71 ft-lb/in²

@Temperature -22.0 °F
cond; ISO 179/1eA
1.20 J/cm²

@Temperature -30.0 °C
5.71 ft-lb/in²

@Temperature -22.0 °F
dry; ISO 179/1eA
1.30 J/cm²

@Temperature 23.0 °C
6.19 ft-lb/in²

@Temperature 73.4 °F
dry; ISO 179/1eA
1.50 J/cm²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
cond; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C
11.1 µin/in-°F
dry; ISO 11359-1/-2
CTE, linear, Transverse to Flow 110 µm/m-°C
61.1 µin/in-°F
dry; ISO 11359-1/-2
Melting Point 220 °C
428 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
dry; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
dry; ISO 75-1/-2
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
dry; IEC 60695-11-10
V-0

@Thickness 0.749 mm
V-0

@Thickness 0.0295 in
dry; IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
cond; IEC 60093
1.00e+15 ohm-cm
1.00e+15 ohm-cm
dry; IEC 60093
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
cond; IEC 60093
Dielectric Constant 3.4

@Frequency 1.00e+6 Hz
3.4

@Frequency 1.00e+6 Hz
dry; IEC 60250
3.5

@Frequency 100 Hz
3.5

@Frequency 100 Hz
dry; IEC 60250
4.0

@Frequency 1.00e+6 Hz
4.0

@Frequency 1.00e+6 Hz
cond; IEC 60250
10

@Frequency 100 Hz
10

@Frequency 100 Hz
cond; IEC 60250
Dissipation Factor 0.0060

@Frequency 100 Hz
0.0060

@Frequency 100 Hz
dry; IEC 60250
0.012

@Frequency 1.00e+6 Hz
0.012

@Frequency 1.00e+6 Hz
dry; IEC 60250
0.070

@Frequency 1.00e+6 Hz
0.070

@Frequency 1.00e+6 Hz
cond; IEC 60250
0.30

@Frequency 100 Hz
0.30

@Frequency 100 Hz
cond; IEC 60250
Comparative Tracking Index 325 V
325 V
dry; IEC 60112