DSM Arnitel® EM402-L Injection Molding; Coating Grade Copolyester Elastomer (North America)  (discontinued **)

Category Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DSM Arnitel® EM402-L Injection Molding; Coating Grade Copolyester Elastomer (North America)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product description: Arnitel® combines the advantages of engineering thermoplastics, being easy to process with excellent mechanical properties, at the same time with the flexibility of rubbers.Arnitel does not require vulcanization. This leads to substantial reductions in part cost. Arnitel can be used over a wide range of temperatures. Arnitel has exceptional fatigue, creep resistance and resistance to oils, greases and many other chemicals.Characteristics of Arnitel:Excellent strength over a wide range of temperaturesExcellent dynamic properties e.g. creep and fatigueHigh heat resistanceExceptional resistance to oils and greasesGood chemical resistanceHigh degree of versatility in processingEasy coloring using masterbatchesSurface quality from high gloss to texturedExcellent heat resistance (long term 165°C)Good electrical insulation propertiesLow moisture absorption, excellent dimensional stabilityEasy flow, fast cooling timesTypical Applications: Automotive: Arnitel® is extensively used in the automotive industry for applications requiring exceptional fatigue resistance and resistance to oil and greases. Examples are: Rack and Pinion Bellows, Constant Velocity Joint Boots (CVJ Boots), Air brake tubings.Arnitel in the Electronic and Consumer Goods Industry: Arnitel® finds enormous potential and is also widely used in the consumer electronics by some of the world's best companies. Arnitel® is the best choice for low noise gears where their exceptional processability without any defects such as flash, makes it the material solution of choice. Arnitel® is also used in highly demanding applications such as in mobile phone antennas.Arnitel® has exceptional flexibility and can perform or even outperform functions that normally require conventional rubbers. Available in a wide range of hardnesses, Arnitel can replace metals, thermoplastics, leather and rubber, often with a reduction in finished part costs.Information provided by DSM.
Physical Properties Metric English Comments
Density 1.10 g/cc
0.0397 lb/in³
ISO 1183
Water Absorption 0.70 %
0.70 %
Sim. to ISO 62
Moisture Absorption at Equilibrium 0.30 %
0.30 %
Humidity Absorption; Sim. to ISO 62
Melt Flow 33 g/10 min

@Load 2.16 kg,
Temperature 230 °C
33 g/10 min

@Load 4.76 lb,
Temperature 446 °F
Calculated from Volume Flow Rate of 30 cm<sup>3</sup>/10 min; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 36
36
3 s; ISO 868
Tensile Strength at Break 25.0 MPa
3630 psi
ISO 527-1/-2
Tensile Strength, Yield 2.40 MPa

@Strain 5.00 %
348 psi

@Strain 5.00 %
ISO 527-1/-2
3.90 MPa

@Strain 10.0 %
566 psi

@Strain 10.0 %
ISO 527-1/-2
6.90 MPa

@Strain 50.0 %
1000 psi

@Strain 50.0 %
ISO 527-1/-2
7.50 MPa

@Strain 100 %
1090 psi

@Strain 100 %
ISO 527-1/-2
Elongation at Break >= 300 %
>= 300 %
ISO 527-1/-2
Elongation at Yield 74 %
74 %
ISO 527-1/-2
Tensile Modulus 0.0500 GPa
7.25 ksi
ISO 527-1/-2
Izod Impact, Notched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 180/1A
Izod Impact, Unnotched (ISO) NB

@Temperature -40.0 °C
NB

@Temperature -40.0 °F
ISO 180/1A
NB

@Temperature -20.0 °C
NB

@Temperature -4.00 °F
ISO 180/1A
Charpy Impact, Notched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eA
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eA
Tensile Impact Strength 218 kJ/m²
104 ft-lb/in²
23°C; ISO 8256/1
Graves Tear Strength 60.0 kN/m
342 pli
without nick; ISO 34
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 220 µm/m-°C

@Temperature 20.0 °C
122 µin/in-°F

@Temperature 68.0 °F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 220 µm/m-°C

@Temperature 20.0 °C
122 µin/in-°F

@Temperature 68.0 °F
ISO 11359-1/-2
Melting Point 195 °C
383 °F
10°C/min; ISO 11357-1/-3
Vicat Softening Point 140 °C
284 °F
50°C/h 10N; ISO 306
Glass Transition Temp, Tg -78.0 °C
-108 °F
10°C/min; ISO 11357-1/-2
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity 5.00e+14 ohm-cm
5.00e+14 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 4.0

@Frequency 1e+6 Hz
4.0

@Frequency 1e+6 Hz
IEC 60250
4.1

@Frequency 100 Hz
4.1

@Frequency 100 Hz
IEC 60250
Dielectric Strength 20.0 kV/mm
508 kV/in
IEC 60243-1
Dissipation Factor 0.0010

@Frequency 100 Hz
0.0010

@Frequency 100 Hz
IEC 60250
0.017

@Frequency 1e+6 Hz
0.017

@Frequency 1e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Coating Yes
High impact or impact modified Yes
Injection molding Yes
U.V. stabilized or stable to weather Yes
Without Fillers Yes