DSM Arnitel® PM581 Polyether Ester Elastomer (European and Asian Grade)

Category Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP , Polyether Ester Elastomer
Manufacturer DSM Engineering Plastics
Trade Name Arnitel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DSM Arnitel® PM581 Polyether Ester Elastomer (European and Asian Grade).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product description: Arnitel® combines the advantages of engineering thermoplastics, being easy to process with excellent mechanical properties, at the same time with the flexibility of rubbers.Arnitel does not require vulcanization. This leads to substantial reductions in part cost. Arnitel can be used over a wide range of temperatures. Arnitel has exceptional fatigue, creep resistance and resistance to oils, greases and many other chemicals.Characteristics of Arnitel:Excellent strength over a wide range of temperaturesExcellent dynamic properties e.g. creep and fatigueHigh heat resistanceExceptional resistance to oils and greasesGood chemical resistanceHigh degree of versatility in processingEasy coloring using masterbatchesSurface quality from high gloss to texturedExcellent heat resistance (long term 165°C)Good electrical insulation propertiesLow moisture absorption, excellent dimensional stabilityEasy flow, fast cooling timesTypical Applications: Automotive: Arnitel® is extensively used in the automotive industry for applications requiring exceptional fatigue resistance and resistance to oil and greases. Examples are: Rack and Pinion Bellows, Constant Velocity Joint Boots (CVJ Boots), Air brake tubings.Arnitel in the Electronic and Consumer Goods Industry: Arnitel® finds enormous potential and is also widely used in consumer electronic companies. Arnitel® is a good choice for low noise gears where their exceptional processability without any defects such as flash, makes it the material solution of choice. Arnitel® is also used in highly demanding applications such as in mobile phone antennas.Arnitel® has exceptional flexibility and can perform or even outperform functions that normally require conventional rubbers. Available in a wide range of hardnesses, Arnitel can replace metals, thermoplastics, leather and rubber, often with a reduction in finished part costs.Information provided by DSM.
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
ISO 1183
Water Absorption 2.5 %
2.5 %
Sim. to ISO 62
Moisture Absorption at Equilibrium 0.40 %
0.40 %
Humidity Absorption; Sim. to ISO 62
Melt Flow 4.305 g/10 min

@Load 2.16 kg,
Temperature 230 °C
4.305 g/10 min

@Load 4.76 lb,
Temperature 446 °F
Calculated from Volume Flow Rate of 3.5 cm<sup>3</sup>/10min.; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 55
55
3s; ISO 868
Tensile Strength at Break 24.5 MPa
3550 psi
ISO 527-1/-2
Tensile Strength, Yield 9.30 MPa

@Strain 5.00 %
1350 psi

@Strain 5.00 %
ISO 527-1/-2
13.1 MPa

@Strain 10.0 %
1900 psi

@Strain 10.0 %
ISO 527-1/-2
17.0 MPa

@Strain 50.0 %
2470 psi

@Strain 50.0 %
ISO 527-1/-2
17.9 MPa

@Strain 100 %
2600 psi

@Strain 100 %
ISO 527-1/-2
Elongation at Break 200 %
200 %
ISO 527-1/-2
Tensile Modulus 0.300 GPa
43.5 ksi
ISO 527-1/-2
Izod Impact, Notched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact, Notched 1.60 J/cm²

@Temperature -30.0 °C
7.61 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 110 µm/m-°C

@Temperature 20.0 °C
61.1 µin/in-°F

@Temperature 68.0 °F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 110 µm/m-°C

@Temperature 20.0 °C
61.1 µin/in-°F

@Temperature 68.0 °F
ISO 11359-1/-2
Melting Point 218 °C
424 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 100 °C
212 °F
ISO 75-1/-2
Vicat Softening Point 105 °C
221 °F
50°C/h 50N; ISO 306
205 °C
401 °F
50°C/h 10N; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 4.4

@Frequency 1e+6 Hz
4.4

@Frequency 1e+6 Hz
IEC 60250
4.7

@Frequency 100 Hz
4.7

@Frequency 100 Hz
IEC 60250
Dielectric Strength 21.0 kV/mm
533 kV/in
IEC 60243-1
Dissipation Factor 0.031

@Frequency 100 Hz
0.031

@Frequency 100 Hz
IEC 60250
0.081

@Frequency 1e+6 Hz
0.081

@Frequency 1e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Film Extrusion Yes
Heat stabilized or stable to heat Yes
High impact or impact modified Yes
Other Extrusion Yes
Profile extrusion Yes
Sheet extrusion Yes
Without Fillers Yes