- DSM Arnitel® VT3104 TPC-ET
DSM Arnitel® VT3104 TPC-ET
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Arnitel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Arnitel® VT3104 TPC-ET.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Extrusion Grade
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 |
| Water Absorption | 7.0 % | 7.0 % | Sim. To ISO 62 |
| Moisture Absorption | 0.400 % | 0.400 % | Sim. To ISO 62 |
| Melt Flow | 13.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
13.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
cm<sup>3</sup>/10min Melt Volume-flow Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 13.1 MPa | 1900 psi | ISO 527-1/-2 |
| Tensile Stress | 4.40 MPa @Strain 10.0 % |
638 psi @Strain 10.0 % |
ISO 527-1/-2 |
| 8.80 MPa @Strain 50.0 % |
1280 psi @Strain 50.0 % |
ISO 527-1/-2 | |
| 10.9 MPa @Strain 100 % |
1580 psi @Strain 100 % |
ISO 527-1/-2 | |
| Elongation at Break | 200 % | 200 % | ISO 527-1/-2 |
| Tensile Modulus | 0.0600 GPa | 8.70 ksi | ISO 527-1/-2 |
| Izod Impact Resistance | NB | NB | ISO 180/1A |
| NB | NB | ISO 180/1A | |
| Charpy Impact, Notched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eA |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 150 µm/m-°C | 83.3 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 150 µm/m-°C | 83.3 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 212 °C | 414 °F | 10°C/min; ISO 11357-1/-3 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Dielectric Constant | 4.4 @Frequency 1.00e+6 Hz |
4.4 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.7 @Frequency 100 Hz |
4.7 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.031 @Frequency 100 Hz |
0.031 @Frequency 100 Hz |
IEC 60250 |
| 0.081 @Frequency 1.00e+6 Hz |
0.081 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Hypalon® 4085 Chlorosulfonated Polyethylene Rubber, Carbon Black Filled Compound
- Ineos 3950 Polypropylene Impact Copolymer
- SABIC Innovative Plastics PC4800 PC (Asia Pacific)
- Seals Eastern 5514 Polyacrylate Rubber
- Styron CALIBREâ„¢ 2061-22 Polycarbonate Resin
- Solvay SIPOMER® BEM Ethoxylated Behenyl Methacrylate
- Vicone High Performance Rubber VicoFluro™ 106F-BK High Performance Fluoroelastomer
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 40 PHR N220 (ISAF) Filler
Copyright © lookpolymers.com All Rights Reserved