DSM Novamid® 1010GN8-30 NAT PA6-GF30 FR
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Novamid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Novamid® 1010GN8-30 NAT PA6-GF30 FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass Reinforced, Flame Retardant, Halogen free
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 1.50 % | 1.50 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 100 MPa | 14500 psi | cond; ISO 527-1/-2 |
| 140 MPa | 20300 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 2.5 % | 2.5 % | dry; ISO 527-1/-2 |
| 3.0 % | 3.0 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 8.50 GPa | 1230 ksi | cond; ISO 527-1/-2 |
| 12.0 GPa | 1740 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 150 MPa | 21800 psi | cond; ISO 178 |
| 220 MPa | 31900 psi | dry; ISO 178 | |
| Flexural Modulus | 6.20 GPa | 899 ksi | cond; ISO 178 |
| 10.2 GPa | 1480 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | 6.30 J/cm² @Temperature 23.0 °C |
30.0 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU |
| 6.70 J/cm² @Temperature 23.0 °C |
31.9 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| 1.60 J/cm² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
dry; IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | dry; IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | cond; IEC 60093 |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
dry; IEC 60250 |
| Dielectric Strength | 23.0 kV/mm | 584 kV/in | dry; IEC 60243-1 |
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
dry; IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | dry; IEC 60112 |