DSM Novamid® 1013GMF H2 NAT/BK37 PA6-GF30
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Novamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Novamid® 1013GMF H2 NAT/BK37 PA6-GF30.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass Reinforced, Heat Stabilized, Injection Molding, Excellent Dimensional Stability
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 2.40 % | 2.40 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in | Sim. To ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | Sim. To ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | cond; ISO 527-1/-2 |
| 135 MPa | 19600 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 3.6 % | 3.6 % | dry; ISO 527-1/-2 |
| 8.2 % | 8.2 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 3.70 GPa | 537 ksi | cond; ISO 527-1/-2 |
| 7.20 GPa | 1040 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 110 MPa | 16000 psi | cond; ISO 178 |
| 210 MPa | 30500 psi | dry; ISO 178 | |
| Flexural Modulus | 3.10 GPa | 450 ksi | cond; ISO 178 |
| 6.60 GPa | 957 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | 5.80 J/cm² @Temperature 23.0 °C |
27.6 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU |
| 7.80 J/cm² @Temperature 23.0 °C |
37.1 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | dry; ISO 75-1/-2 |