DSM Stanyl® 46HF5050 Nylon 46-50% Glass Reinforced (European and Asian Grade) (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 46 , Nylon 46, Glass Fiber Reinforced
Manufacturer DSM Engineering Plastics
Trade Name Stanyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DSM Stanyl® 46HF5050 Nylon 46-50% Glass Reinforced (European and Asian Grade) (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temperatures Excellent resistance to wear and low friction Outstanding flow for easy processing and exceptional design freedomStanyl High Flowgrades that match the best flowing LCPs while maintaining a high level of mechanical propertiesKey Applications: Automotive: Powertrain components, Charge-air coolers, EPS and ETC gears, Motor Sensors, Auto connectors, Chain tensionersE&E: Connectors, Microswitches, Bobbins, Memory modules, Motor components, Industrial, Specialty films and fibers, Consumer appliancesInformation provided by DSM.
Physical Properties Metric English Comments
Density 1.87 g/cc
0.0676 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 1.1 %
1.1 %
Humidity Absorption; Sim. to ISO 62
Viscosity Test 70 cm³/g
70 cm³/g
Viscosity Number
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 200 MPa
29000 psi
ISO 527-1/-2
Elongation at Break 1.5 %
1.5 %
ISO 527-1/-2
Tensile Modulus 18.0 GPa
2610 ksi
ISO 527-1/-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C

@Temperature 20.0 °C
 11.1 µin/in-°F

@Temperature 68.0 °F
 ISO 11359-1/-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature 20.0 °C
 44.4 µin/in-°F

@Temperature 68.0 °F
 ISO 11359-1/-2
Melting Point 295 °C
563 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 290 °C
554 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 290 °C
554 °F
ISO 75-1/-2
Vicat Softening Point 290 °C
554 °F
50°C/h 50N; ISO 306
Glass Transition Temp, Tg 75.0 °C
167 °F
Glass Transition Temperature (10°C/min); ISO 11357-1/-2
UL RTI, Electrical 140 °C

@Thickness 1.50 mm
 284 °F

@Thickness 0.0591 in
 UL746B
140 °C

@Thickness 0.750 mm
 284 °F

@Thickness 0.0295 in
 UL746B
UL RTI, Mechanical with Impact 110 °C

@Thickness 0.750 mm
 230 °F

@Thickness 0.0295 in
 UL746B
125 °C

@Thickness 1.50 mm
 257 °F

@Thickness 0.0591 in
 UL746B
UL RTI, Mechanical without Impact 120 °C

@Thickness 0.750 mm
 248 °F

@Thickness 0.0295 in
 UL746B
125 °C

@Thickness 1.50 mm
 257 °F

@Thickness 0.0591 in
 UL746B
Flammability, UL94 V-0

@Thickness 0.400 mm
 V-0

@Thickness 0.0157 in
 IEC 60695-11-10
V-0

@Thickness 1.60 mm
 V-0

@Thickness 0.0630 in
 IEC 60695-11-10
Glow Wire Test 825 °C

@Thickness 0.750 mm
 1520 °F

@Thickness 0.0295 in
 Glow Wire Ignition Temperature; IEC 60695-2-13
925 °C

@Thickness 3.00 mm
 1700 °F

@Thickness 0.118 in
 Glow Wire Ignition Temperature; IEC 60695-2-13
960 °C

@Thickness 0.750 mm
 1760 °F

@Thickness 0.0295 in
 Glow Wire Flammability Index; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
 1760 °F

@Thickness 0.118 in
 Glow Wire Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 250 - 399 V
250 - 399 V
PLC 2; UL 746A
Descriptive Properties Value Comments
Flame Retardant Yes
Flame Retarding Agent Yes
Heat stabilized or stable to heat Yes
Injection molding Yes
Lubricants Yes
Platable Yes
Release Agent Yes
With Fillers Yes