Daelim H&L Plavis-G40 DF 40% Graphite Filled Aromatic Polyimide Bearing

Category Polymer , Thermoset , Polyimide, TS
Manufacturer Daelim H&L Super Engineering Plastics
Trade Name Plavis-G40
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Daelim H&L Plavis-G40 DF 40% Graphite Filled Aromatic Polyimide Bearing.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Direct Formed. Plavis-G-40: Graphite 40 wt% filled, Self lubricating grade with low thermal expansion.General Plavis information for all grades:PLAVIS polyimide has nitrogen bonded to 3 carbons is the critical part of the chain and imparts the plastic with remarkable features and benefits. PLAVIS is available as raw material or as molded parts, plates, and rods. PLAVIS isostatic molded rods have uniform properties in all directions. Properties:One of the highest temperature plastics in the world with a continuous operating temperature of 300?. Well suited for cryogenic conditionsRetains high tensile strength and modulus even at high temperatures. Will not crack or creep under load.Lowest out-gassing of any plastic at 300?. Will not contaminate vacuum chamber process or products.Grades are available for use at 1 million psi-fpm PV limit with lubrication, 300,000 psi-fpm PV limit without lubrication. Stable friction level.Filled grades resistivity is tailorable.Machines like brass-tiny and intricate features can be produced without cracking. Can be lapped to mirror finish.Applications: Flat Panel Display/Solar Cells:: Drying oven (HP/CP, Baking, IR) Glass support pins, Glass holders, Rollers; Cleaning EUV roller, Bearing; PVD/CVD Insulation parts Insert, Clamp, Bush, Caps, Susceptor pin, Ball bearing etc.; Etcher Screw, bolts. and Others Probe unit, station parts Semiconductor: Wafer Processing Wafer clamp rings, Insulators, Screw & Fasteners, Vacuum pads, Alignment pins; Wafer handling, guides, and carriers, Vacuum pick up strips; IC handling & testing Die pick up collects, Test socket insulator General Industry: Hot runner system Seal caps, Insulators; Plasma cutting torches parts Swirl rings, Insulator, Caps.; Heat resistance materials Bottle grippers, Conveyor tips; Scientific consumable parts GC/Mass ferrules, HPLC valve rotors; Textile Machines Valve seat, Bearing, Shedder Bushing Automotive / Transportation:Transmissions Thrust Washers, Seal Rings, Valve Seats, Transmission Valve Balls, Check Valves; Electrical Motors Bushings, Washers, Thrust Plugs; Brakes Wear Pads, Valve Seats and Balls in ABS Systems; Fuel Systems Bushings, Seal Rings, Band Springs, Valve Seats; Turbo Chargers Ball Bearing Retainers, Wastegate Bushings; Vacuum Pump Vanes, Engine Belt Tensioners, Rubbing Blocks, Door Hinge Bushings, Gear Stick Rollers, Ignition Distributors, Constant Friction Pads for Split-Flywheels Aerospace/Aircraft: Compressor Variable Vane Bushings and Washers, Aircraft Fan Thrust Reverser, Fan Blade Wear Strips, Locking Insert Nut, Fuel Line Spacer, Reciprocating Shaft Seal for Jet Engine Afterbunner Actuating SystemInformation provided by Daelim H&L
Physical Properties Metric English Comments
Specific Gravity 1.56 g/cc
1.56 g/cc
ASTM D792
Mechanical Properties Metric English Comments
Hardness, Rockwell M 65.0 - 80.0
65.0 - 80.0
ASTM D785
Tensile Strength, Ultimate 53.9 MPa
7820 psi
ASTM D1708
26.5 MPa

@Temperature 260 °C
3840 psi

@Temperature 500 °F
ASTM D1708
Elongation at Break 3.50 %
3.50 %
ASTM D1708
2.50 %

@Temperature 260 °C
2.50 %

@Temperature 500 °F
ASTM D1708
Flexural Strength 63.7 MPa
9240 psi
ASTM D790
39.2 MPa

@Temperature 260 °C
5690 psi

@Temperature 500 °F
ASTM D790
Flexural Modulus 4.854 GPa
704.0 ksi
ASTM D790
2.746 GPa

@Temperature 260 °C
398.3 ksi

@Temperature 500 °F
ASTM D790
Compressive Strength 24.5 MPa

@Strain 1.00 %
3550 psi

@Strain 1.00 %
ASTM D695
93.2 MPa

@Strain 10.0 %
13500 psi

@Strain 10.0 %
ASTM D695
Compressive Modulus 2.648 GPa
384.1 ksi
ASTM D695
Coefficient of Friction 0.180
0.180
PV=10 kg/cm² · m/sec (0.98 Mpa·m/sec)
Thermal Properties Metric English Comments
CTE, linear 25.0 µm/m-°C

@Temperature 23.0 - 260 °C
13.9 µin/in-°F

@Temperature 73.4 - 500 °F
ASTM D696
Maximum Service Temperature, Air 370 °C
698 °F
50% tensile strength reduction at 360 hours
Deflection Temperature at 1.8 MPa (264 psi) 360 °C
680 °F
Decomposition Temperature 520 °C
968 °F
50wt% reduction after 239 min
614 °C
1140 °F
short term
Flammability, UL94 V-0
V-0
Oxygen Index 54.0 %
54.0 %