Daikin DAI-EL G-603 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 71% Fluorine Content

Category Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer Daikin Industries
Trade Name DAI-EL
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Daikin DAI-EL G-603 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 71% Fluorine Content.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Offers minimal compression set and excellent sealing. The terpolymer type is able to withstand polarized solvents to realize a wide range of application.Information provided by Daikin Industries.
Physical Properties Metric English Comments
Specific Gravity 1.92 g/cc
1.92 g/cc
at 25°C
Mooney Viscosity 31

@Temperature 121 °C
31

@Temperature 250 °F
ML 1+10
Mechanical Properties Metric English Comments
Hardness, Shore A 77
77
Peak value, at 25°C
Tensile Strength at Break 14.0 MPa
2030 psi
Tensile Strength, Yield 3.70 MPa

@Strain 100 %
537 psi

@Strain 100 %
Elongation at Break 280 %
280 %
Tear Strength 21.0 kN/m
120 pli
at 25°C
Compression Set 36 %
36 %
70 hours at 25°C
30 %

@Temperature 100 °C
30 %

@Temperature 212 °F
70 hours
35 %

@Temperature 175 °C
35 %

@Temperature 347 °F
70 hours
60 %

@Temperature 200 °C
60 %

@Temperature 392 °F
70 hours
Thermal Properties Metric English Comments
Minimum Service Temperature, Air -8.00 °C
17.6 °F
TR test, TR10
-4.80 °C
23.4 °F
Gehman torsion test, T10
-2.00 °C
28.4 °F
TR test, TR70
-1.30 °C
29.7 °F
Gehman torsion test, T2
Brittleness Temperature -14.0 °C
6.80 °F
Processing Properties Metric English Comments
Processing Temperature 170 °C
338 °F
Cure Measuring Temperature
Cure Time 4.40 min
0.0733 hour
Curelastmeter